Eurostar Starflam RF023P PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer	Eurostar Engineering Plastics
Trade Name	Starflam
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eurostar Starflam RF023P PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Starflam RF0023P is a Flame Retardant, Halogen Free, Red Phosphorous Free, Glass Reinforced Polyamide 66/6 Injection Molding (also known as Starflam PA66C U2 Z23)Information provided by Eurostar.

Physical Properties	Metric	English	Comments
Density	1.72 g/cc	0.0621 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm @Thickness 4.00 mm	0.0020 - 0.0040 in/in @Thickness 0.157 in	E2P method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	94.0 MPa	13600 psi	5 mm/min; ISO 527
Elongation at Break	1.4 %	1.4 %	5 mm/min; ISO 527
Flexural Strength	139 MPa	20200 psi	2 mm/min; ISO 178
Flexural Modulus	9.50 GPa	1380 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	2.00 kJ/m²	0.952 ft-lb/in²	80x10x4; ISO 179/1eA
Izod Impact, Unnotched (ISO)	20.0 kJ/m²	9.52 ft-lb/in²	80x10x4; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	192 °C	378 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
Glow Wire Test	960 °C @Thickness 1.60 mm	1760 °F @Thickness 0.0630 in	IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English
Zone 1	270 - 280 °C	518 - 536 °F
Zone 2	275 - 285 °C	527 - 545 °F
Zone 3	280 - 300 °C	536 - 572 °F
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.20 %	0.20 %