Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX06010 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 1.9 % @Temperature 23.0 °C, Time 86400 sec |
1.9 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Thickness 4.00 mm |
0.0035 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 81.0 MPa | 11700 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | >= 4.3 % | >= 4.3 % | Flexural, 2 mm/min; ISO 178 |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 133 MPa | 19300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 137 MPa | 19900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-1038 Natural MA PVC Compound
- FKuR Kunststoff Terralene® WF 3516 Biobased Polyethylene
- Intercontinental Polymers 1140 Bicomponent HDPE/PET Fiber Type - 10 X 2 Inches
- Haysite 20000 Polyester BMC, 15% Glass Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Branched (Asia Pacific)
- A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene
- China Tungsten WC 96 Tungsten Carbide Powder
- AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition TH 1050
- 3M Scotch® 5912 Cellophane Tape
- Overview of materials for Cellulose Acetate Propionate, Molded
Copyright © lookpolymers.com All Rights Reserved