- Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded
Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PK0069 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known as Starflam PA6 30E6 Z88)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Flexural, 2 mm/min; ISO 178 | |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 101 MPa | 14600 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 101 MPa | 14600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90049 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP LUBRICOMP KP004AXP POM (Europe-Africa-Middle East)
- Sharadaa Ceramics Sharada RFC-95 Gel Bonded Castables
- Struktol STRUKSILON 8005 Silicone Stabilizer for PU-Rigid Foam
- Toyobo GLAMIDE® NB-5550 Nylon/Olefin
- Chengdu Polyster 10 LPI Lenticular Lens Sheet, PS
- Arkema Group Rilsan® BZM 8 NOIR TL Nylon 11, 8% Glass Fiber Filled (Conditioned)
- Alliance N-40H Neodymium Iron Boron Magnetic Material
- DuPont Bexloy® AXW502NC010 Modified Ionomer Resin (discontinued **)
- Master Bond Supreme 3ANHT Epoxy Adhesives for Bonding Stainless Steel
Copyright © lookpolymers.com All Rights Reserved