Eurostar Starflam M10004A PP, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam M10004A PP, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam M10004A is an Unfilled Halogen Free Flame Retardant PP injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 4.00 mm |
0.018 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.2 % | 4.2 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 44.0 MPa | 6380 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 108 µm/m-°C @Temperature 23.0 - 60.0 °C |
60.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature 23.0 - 60.0 °C |
60.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 190 °C | 356 - 374 °F | |
| Zone 2 | 190 - 200 °C | 374 - 392 °F | |
| Zone 3 | 190 - 200 °C | 374 - 392 °F | |
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Nye Lubricants 605A (SO) Synthetic Oil
- PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer
- Saint-Gobain Spectrosil® 2200 Optical Fused Quartz
- TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin
- A. Schulman COMTUF® 420 Impact Modified PBT
- Eagle Brass 194 HSM® Copper, 1/2 Hard
- Covestro Texin® 285 Urethane Thermoplastic Elastomer
- ExxonMobil HDPE HD 6704.18 High Density Polyethylene Copolymer Resin
- Ensinger Tecamid® MDS® Molybdenum Disulfide Filled Nylon (PA)
Copyright © lookpolymers.com All Rights Reserved