PolyOne Edgetek® AS-1000 HI Acrylonitrile Butadiene Styrene (ABS) (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-1000 HI Acrylonitrile Butadiene Styrene (ABS)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:High ImpactPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 40.7 MPa | 5900 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 3.26 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
6.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 91.8 µm/m-°C @Temperature 20.0 °C |
51.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.6 °C | 204 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C | 195 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 249 °C | 440 - 480 °F | Molding |
| Mold Temperature | 26.7 - 60.0 °C | 80.0 - 140 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Haveg Havaflex T.A.-117 Phenolic, Trowelable Ablative Coating
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction
- Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc
- Samsung Cheil Industries Starex® WR-9370 ASA, Unreinforced Heat Resistant
- Styron XZ 91982.00 Carboxylated SB
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- Dow Corning SILASTIC® 3498 MOULD MAKING BASE & 96 CURING AGENT
- ExxonMobil 220 Mobilgear SHC XMP Series
- Ametek P434L P/M Stainless Steel, Sintered from 6.2 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved