- Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding
Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam AFR560B5 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -40.0 °C |
0.952 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Vicat Softening Point | 257 °C | 495 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 285 °C | 518 - 545 °F | |
| Melt Temperature | 270 - 285 °C | 518 - 545 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP640T Injection Molding Grade Polypropylene
- Huntsman PE1356 EVA Film Extrusion (discontinued **)
- DSM Akulon® S223-TP4 Impact Modified Nylon 66 (European Grade) (Dry) (discontinued **)
- Inno-Comp INNOPOL® CS 2-8000 Polypropylene Block-Copolymer
- Lubriplate GR-132 Portable Tool Grease Specialty Lubricant and Grease
- Lanxess Pocan® KU 2-7503/1 000000 PBT
- Kostat G148BK TAB Spacer Reels
- Teknor Apex Monprene® MP-1848K Thermoplastic Elastomer
- ExxonMobil Mobil Rarus 826
- ArcelorMittal 04 High formability steel for drawing, Cold rolled
Copyright © lookpolymers.com All Rights Reserved