Eurostar Staramide RFC16 PA66/6, Glass/Carbon Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RFC16 PA66/6, Glass/Carbon Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RFC16 is a Glass Fiber and Carbon Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as STAR C PA66 C 303VY Z3)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 141 MPa | 20500 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 91.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB OTM-17 Organo Tin Stabilizer
- SABIC Innovative Plastics Lexan® SLD3000 PC (Asia Pacific)
- Honeywell Capran® Emblem™ 2500 Bi-Axially Oriented Nylon Film
- SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66
- SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific)
- A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene
- Total PSI 2451 High Heat Resistance Impact Polystyrene
- EMS-Griltech Grilon® BM 24R Nylon 6 Monofilament (Medium-Set)
Copyright © lookpolymers.com All Rights Reserved