Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RF00ASXA is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.4 GPa | 2230 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 305 MPa | 44200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 14.1 GPa | 2050 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Plasma Coatings 900 Surface Material
- Plastcom SLOVAMID 66 BT Polyamide 66
- Polymax® Maxelast® P1776 TPE, PP Overmold or Standalone use
- A. Schulman POLYBATCH™ Blue 4021 Concentrate Based in Polyethylene
- Wellman Wellamid® MRGF25/15 22H-NBK1/WE-1364 40% Mineral/Glass Reinforced Nylon 66
- Williams Advanced Alloys WS243 Solder
- DuPont™ Nomex® 410 Paper, 15 mil Nominal Thickness
- BASF Ultramid® 8202 PA6 (Dry)
- BASF Ultramid® A3HG3 PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved