- Eurostar Staramide PF00AS PA6, 50% Glass Fiber Filled, Injection Molded
Eurostar Staramide PF00AS PA6, 50% Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PF00AS PA6, 50% Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PF00AS is a 50% Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0035 cm/cm @Thickness 4.00 mm |
0.0015 - 0.0035 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 220 MPa | 31900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 300 MPa | 43500 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | 80x10x4; ISO 180/1U |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 260 - 280 °C | 500 - 536 °F | |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG38N ABS (Asia Pacific)
- Polykemi AB POLYlux 4010 MP PC/PBT-Blend
- SABIC Innovative Plastics LNP Faradex DS0036IP PC (Europe-Africa-Middle East)
- Chevron Phillips 6109DK LLDPE Blown Film Resin, Butene Copolymer (discontinued **)
- Ravago Manufacturing Americas Enviramid™ N1335HL BK Nylon 6/6
- Multibase Multi-Flex® A 6221 E Black TPE Thermoplastic Elastomer
- Styron CALIBREâ„¢ 302EP-22 Polycarbonate Resin
- Supreme Petrochem SC 203EL General Purpose Polystyrene
- Washington Penn Homopolymer Polypropylene 30% Talc Filled
- Barlog Plastics KEBAFORM C 520.0 POM Copolymer unreinforced
Copyright © lookpolymers.com All Rights Reserved