Eurostar Staramide AG8 PA66, 40% Glass Fiber Reinforced, Injection Molding

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide AG8 PA66, 40% Glass Fiber Reinforced, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide AG8 is a 40% Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Moisture Absorption 0.900 %

@Temperature 23.0 °C
 0.900 %

@Temperature 73.4 °F
 50% RH; ISO 62
Water Absorption at Saturation 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, Rockwell L 114
114
ISO 2039-2
Tensile Strength at Break 205 MPa
29700 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 12.0 GPa
1740 ksi
1 mm/min; ISO 527
Flexural Strength 295 MPa
42800 psi
2 mm/min; ISO 178
Flexural Modulus 1.10 GPa
160 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
12.0 kJ/m²

@Temperature -20.0 °C
 5.71 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
12.0 kJ/m²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 80x10x4; ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 11.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 73.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 40.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 258 °C
496 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 258 °C
496 °F
B/120; ISO 306
260 °C
500 °F
B/50; ISO 306
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Flame Spread 2.00 mm/min

@Thickness 2.00 mm
 0.0787 in/min

@Thickness 0.0787 in
 FMVSS Burning Speed
6.00 mm/min

@Thickness 2.00 mm
 0.236 in/min

@Thickness 0.0787 in
 FMVSS Burning Speed
Oxygen Index 27 %
27 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.4

@Frequency 50.0 - 60.0 Hz
 3.4

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0068

@Frequency 50.0 - 60.0 Hz
 0.0068

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 350 V
350 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 260 - 280 °C
500 - 536 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 290 °C
518 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %