- Hexcel® HexPly® F522 Epoxy Resin, T2C145 Carbon Tape
Hexcel® HexPly® F522 Epoxy Resin, T2C145 Carbon Tape
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Hexcel® HexPly® F522 Epoxy Resin, T2C145 Carbon Tape.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: T_145-12"-F522; Various Fibers; (145 g/m2)Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.7 MPa <br>@Temperature 24.0 °C |
2860 psi <br>@Temperature 75.2 °F |
Dry |
| 1758 MPa <br>@Temperature -55.0 °C |
255000 psi <br>@Temperature -67.0 °F |
Dry | |
| 1793 MPa <br>@Temperature 71.0 °C |
260100 psi <br>@Temperature 160 °F |
Dry | |
| Tensile Modulus | 131.7 GPa <br>@Temperature 24.0 °C |
19100 ksi <br>@Temperature 75.2 °F |
Dry |
| 132.4 GPa <br>@Temperature 71.0 °C |
19200 ksi <br>@Temperature 160 °F |
Dry | |
| 140 GPa <br>@Temperature -55.0 °C |
20300 ksi <br>@Temperature -67.0 °F |
Dry | |
| Compressive Yield Strength | 848 MPa <br>@Temperature 71.0 °C |
123000 psi <br>@Temperature 160 °F |
Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 1117 MPa <br>@Temperature 24.0 °C |
162000 psi <br>@Temperature 75.2 °F |
Dry | |
| Compressive Modulus | 119.3 GPa <br>@Temperature 71.0 °C |
17300 ksi <br>@Temperature 160 °F |
Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 133.1 GPa <br>@Temperature 24.0 °C |
19300 ksi <br>@Temperature 75.2 °F |
Dry | |
| Shear Strength | 38.6 MPa <br>@Temperature 71.0 °C |
5600 psi <br>@Temperature 160 °F |
Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 82.0 MPa <br>@Temperature 24.0 °C |
11900 psi <br>@Temperature 75.2 °F |
Short Beam, Dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Dry Resin Content (%) | 37-41 | Prepreg |
| Fiber Volume (%) | 0.014 | Laminate |
| Flow (%) | 4-16 | |
| Wet Resin Content (%) | 52 | Laminate |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP ZI001 PPE+PS
- A. Schulman FORMION™ FI 342 Ionomer
- Trelleborg B569 Nitrile Rubber
- BASF E-por® 0.02 g/cc Density; Styrene and Ethylene (Europe)
- BASF Heligoen® Green L 8730 Color Additive
- Asahi Kasei Thermylene® P6-20FG-0753 20% Glass Fiber Reinforced, Heat Stabilized
- 3M Scotchcal™ 1000-57 Graphic Film
- 3M Scotchlite™ 680CR-71 Removable Reflective Graphic Film with Comply™ Adhesive
- DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66 (Unverified Data**)
- Eastman Tenite 358-15 CAP Cellulose Acetate Propionate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved