| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA6 D83 PA6, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA6 D83 is a PTFE/Proprietary Additive Lubricated, Unreinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 - 0.022 cm/cm @Thickness 4.00 mm |
0.018 - 0.022 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 245 °C | 455 - 473 °F | |
| Zone 3 | 240 - 260 °C | 464 - 500 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1704 Polypropylene Homopolymer, Stretched Tape Grade
- PTS SAN-82TR SAN Resin
- Kolon KOCETAL® LW301 Wear Modified Acetal Resin
- LG Chemical 81HF SAN Resin
- Solvay TECHNYLSTARâ„¢ S 216 V35 PA6, 35% glass filled, Conditioned
- Plenco 4527 Phenolic, Granular, Injection Molded
- Unitika elitel UE3800 Polyester, Pellet
- Dow Corning SILASTIC® LSR 9682-50 PARTS A&B
- CMW® ELKONIUM 305 platinum based alloy
Copyright © lookpolymers.com All Rights Reserved