Entec Hylex® P1025L1 HB Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hylex® P1025L1 HB Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in North America Features: General Purpose Agency Ratings: FDA 21 CFR 177.1580 RoHS Compliant Form: Pellets Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 72 | 72 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 1.0 % @Thickness 3.17 mm |
1.0 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 88 % @Thickness 3.17 mm |
88 % @Thickness 0.125 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- MV Labs HO300 Ho2(CO3)3·xH2O Holmium carbonate hydrate
- Multibase Multibatch® MP 52206 Sheet Extrusion
- Zeon Chemicals Quintone® K100 Aliphatic Hydrocarbon Resin
- Arkema Group Solarkote® PB Acrylic
- Asia Technology Pioneers CAN 102 Acrylic Hi-Compound Resin
- Eurotec® Tecomid® NB40 NL IH PA6, impact modified, natural
- Fainplast Compounds KLT 75/G Flexible PVC, Sheathing Transparent Cables Lead Free
- Bulk Molding Compounds BMC T40-4020-AQ High Strength Arc Quenching Molding Compound
Copyright © lookpolymers.com All Rights Reserved