Outokumpu 253MA® High Temperature Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 253MA® High Temperature Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used between 600-850°C can lead to reduced impact toughness at room temperature.Applications: Heat and creep resistance. For use over 550°C for equipment and components within: Iron, steel, and non-ferrous industriesEngineering industryEnergy conservation plantsCement industryAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 7.80 g/cc
0.282 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 700 MPa
102000 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
360 MPa

@Temperature 700 °C
 52200 psi

@Temperature 1290 °F
 EN min.
445 MPa

@Temperature 600 °C
 64500 psi

@Temperature 1110 °F
 EN min.; EN 10002-5
495 MPa

@Temperature 500 °C
 71800 psi

@Temperature 932 °F
 EN min.; EN 10002-5
530 MPa

@Temperature 400 °C
 76900 psi

@Temperature 752 °F
 EN min.; EN 10002-5
535 MPa

@Temperature 300 °C
 77600 psi

@Temperature 572 °F
 EN min.; EN 10002-5
545 MPa

@Temperature 200 °C
 79000 psi

@Temperature 392 °F
 EN min.; EN 10002-5
585 MPa

@Temperature 100 °C
 84800 psi

@Temperature 212 °F
 EN min.; EN 10002-5
630 MPa

@Temperature 50.0 °C
 91400 psi

@Temperature 122 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 370 MPa

@Strain 0.200 %
 53700 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
410 MPa

@Strain 1.00 %
 59500 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
130 MPa

@Strain 0.200 %,
Temperature 700 °C
 18900 psi

@Strain 0.200 %,
Temperature 1290 °F
 EN min.
140 MPa

@Strain 0.200 %,
Temperature 600 °C
 20300 psi

@Strain 0.200 %,
Temperature 1110 °F
 EN min.; EN 10002-5
150 MPa

@Strain 0.200 %,
Temperature 500 °C
 21800 psi

@Strain 0.200 %,
Temperature 932 °F
 EN min.; EN 10002-5
155 MPa

@Strain 1.00 %,
Temperature 700 °C
 22500 psi

@Strain 1.00 %,
Temperature 1290 °F
 EN min.
160 MPa

@Strain 0.200 %,
Temperature 400 °C
 23200 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
170 MPa

@Strain 1.00 %,
Temperature 600 °C
 24700 psi

@Strain 1.00 %,
Temperature 1110 °F
 EN min.; EN 10002-5
170 MPa

@Strain 0.200 %,
Temperature 300 °C
 24700 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
180 MPa

@Strain 1.00 %,
Temperature 500 °C
 26100 psi

@Strain 1.00 %,
Temperature 932 °F
 EN min.; EN 10002-5
185 MPa

@Strain 0.200 %,
Temperature 200 °C
 26800 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
190 MPa

@Strain 1.00 %,
Temperature 400 °C
 27600 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
200 MPa

@Strain 1.00 %,
Temperature 300 °C
 29000 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
215 MPa

@Strain 1.00 %,
Temperature 200 °C
 31200 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
230 MPa

@Strain 0.200 %,
Temperature 100 °C
 33400 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
265 MPa

@Strain 1.00 %,
Temperature 100 °C
 38400 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
280 MPa

@Strain 0.200 %,
Temperature 50.0 °C
 40600 psi

@Strain 0.200 %,
Temperature 122 °F
 EN min.; EN 10002-5
315 MPa

@Strain 1.00 %,
Temperature 50.0 °C
 45700 psi

@Strain 1.00 %,
Temperature 122 °F
 EN min.; EN 10002-5
Elongation at Break 50 %
50 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Rupture Strength 4.00 MPa

@Temperature 1100 °C,
Time 3.60e+7 sec
 580 psi

@Temperature 2010 °F,
Time 10000 hour
7.00 MPa

@Temperature 1000 °C,
Time 3.60e+7 sec
 1020 psi

@Temperature 1830 °F,
Time 10000 hour
13.0 MPa

@Temperature 900 °C,
Time 3.60e+7 sec
 1890 psi

@Temperature 1650 °F,
Time 10000 hour
18.0 MPa

@Temperature 850 °C,
Time 3.60e+7 sec
 2610 psi

@Temperature 1560 °F,
Time 10000 hour
27.0 MPa

@Temperature 800 °C,
Time 3.60e+7 sec
 3920 psi

@Temperature 1470 °F,
Time 10000 hour
41.0 MPa

@Temperature 750 °C,
Time 3.60e+7 sec
 5950 psi

@Temperature 1380 °F,
Time 10000 hour
63.0 MPa

@Temperature 700 °C,
Time 3.60e+7 sec
 9140 psi

@Temperature 1290 °F,
Time 10000 hour
98.0 MPa

@Temperature 650 °C,
Time 3.60e+7 sec
 14200 psi

@Temperature 1200 °F,
Time 10000 hour
157 MPa

@Temperature 600 °C,
Time 3.60e+7 sec
 22800 psi

@Temperature 1110 °F,
Time 10000 hour
250 MPa

@Temperature 550 °C,
Time 3.60e+7 sec
 36300 psi

@Temperature 1020 °F,
Time 10000 hour
Modulus of Elasticity 200 GPa
29000 ksi
RT
120 GPa

@Temperature 1000 °C
 17400 ksi

@Temperature 1830 °F
163 GPa

@Temperature 500 °C
 23600 ksi

@Temperature 932 °F
Thermal Properties Metric English Comments
CTE, linear 18.2 µm/m-°C

@Temperature 500 °C
 10.1 µin/in-°F

@Temperature 932 °F
19.5 µm/m-°C

@Temperature 1000 °C
 10.8 µin/in-°F

@Temperature 1830 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
0.580 J/g-°C

@Temperature 500 °C
 0.139 BTU/lb-°F

@Temperature 932 °F
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
21.2 W/m-K

@Temperature 500 °C
 147 BTU-in/hr-ft²-°F

@Temperature 932 °F
29.0 W/m-K

@Temperature 1000 °C
 201 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Maximum Service Temperature, Air 1100 °C
2010 °F
Dry Air
Component Elements Properties Metric English Comments
Carbon, C 0.090 %
0.090 %
Cerium, Ce 1.6 %
1.6 %
Chromium, Cr 21 %
21 %
Iron, Fe 64.54 %
64.54 %
Nickel, Ni 11 %
11 %
Nitrogen, N 0.17 %
0.17 %
Silicon, Si 1.6 %
1.6 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000840 ohm-cm
0.0000840 ohm-cm
RT
Processing Properties Metric English Comments
Annealing Temperature 900 °C
1650 °F
Stress Relief Annealing (min. 0.5 h)
1020 - 1120 °C
1870 - 2050 °F
Solution Annealing