LATI Latilub 66-15T K/30 PA66, 30% Carbon Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latilub 66-15T K/30 PA66, 30% Carbon Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
<br>@Temperature 150 °C
 15200 psi
<br>@Temperature 302 °F
125 MPa
<br>@Temperature 120 °C
 18100 psi
<br>@Temperature 248 °F
140 MPa
<br>@Temperature 90.0 °C
 20300 psi
<br>@Temperature 194 °F
170 MPa
<br>@Temperature 60.0 °C
 24700 psi
<br>@Temperature 140 °F
230 MPa
<br>@Temperature 23.0 °C
 33400 psi
<br>@Temperature 73.4 °F
Elongation at Break 1.9 %
<br>@Temperature 23.0 °C
 1.9 %
<br>@Temperature 73.4 °F
2.5 %
<br>@Temperature 60.0 °C
 2.5 %
<br>@Temperature 140 °F
3.2 %
<br>@Temperature 90.0 °C
 3.2 %
<br>@Temperature 194 °F
3.5 %
<br>@Temperature 120 °C
 3.5 %
<br>@Temperature 248 °F
3.8 %
<br>@Temperature 150 °C
 3.8 %
<br>@Temperature 302 °F
Tensile Modulus 8.30 GPa
<br>@Temperature 150 °C
 1200 ksi
<br>@Temperature 302 °F
11.3 GPa
<br>@Temperature 120 °C
 1640 ksi
<br>@Temperature 248 °F
16.0 GPa
<br>@Temperature 90.0 °C
 2320 ksi
<br>@Temperature 194 °F
22.5 GPa
<br>@Temperature 60.0 °C
 3260 ksi
<br>@Temperature 140 °F
24.0 GPa
<br>@Temperature 23.0 °C
 3480 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²
<br>@Temperature -20.0 °C
 19.0 ft-lb/in²
<br>@Temperature -4.00 °F
5.00 J/cm²
<br>@Temperature 23.0 °C
 23.8 ft-lb/in²
<br>@Temperature 73.4 °F
Charpy Impact, Notched 0.600 J/cm²
<br>@Temperature -20.0 °C
 2.86 ft-lb/in²
<br>@Temperature -4.00 °F
0.800 J/cm²
<br>@Temperature 23.0 °C
 3.81 ft-lb/in²
<br>@Temperature 73.4 °F
Coefficient of Friction, Dynamic 0.19
0.19
Coefficient of Friction, Static 0.25
0.25
K (wear) Factor 15.0 x 10<sup>-8</sup> mm³/N-M
7.45 x 10<sup>-10</sup> in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 255 °C
<br>@Load 5.00 kg
 491 °F
<br>@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C
<br>@Time 10800 sec
 194 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa