Eastman Tritan TX1500HF Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Eastman Chemical |
| Trade Name | Tritan |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tritan TX1500HF Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eastman Tritan TX1500HF is a high flow grade of Eastman Tritan. Eastman Tritan TX1500HF has viscosity reductions of 40-50% relative to Eastman Tritan copolyester TX1000. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance.Application/UsesAppliancesConsumer goodsDurable goodsHousewaresKey AttributesEase of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceGood flowabilityGood heat resistanceOutstanding impact resistanceQuick cycle timesTypical properties as listed are from preliminary data. Information was provided by Eastman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 210 % | 210 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.575 GPa | 228.4 ksi | ASTM D638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 1.575 GPa | 228.4 ksi | ASTM D790 |
| Izod Impact, Notched | 8.60 J/cm | 16.1 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes | Repeated use food contact articles |
| NSF | Yes | Yes | Food equipment materials; NSF/ANSI Standard 51 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 282 °C | 500 - 540 °F | |
| Mold Temperature | 38.0 - 66.0 °C | 100 - 151 °F | |
| Drying Temperature | 88.0 °C | 190 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GF 1815 PVC/Nitrile Alloy
- NIZHNEKAMSKNEFTEKHIM PP 4215M (EP1X35F) Propylene and Ethylene Copolymer
- LG Chemical Lupoy 1603-03 Polycarbonate Resin
- Karina 300-40/236 Green PVC Compound
- SGL Carbon Group EK 2230 Carbon Graphite
- Polyram PlusTek PA804 Nylon 6.6 for Injection Molding, Impact Modified
- ERG Aerospace Duocel® Silicon Carbide Foam
- Arlon R33670N004 0.004" (0.102 mm) Uncured Silicone Rubber with K2030 PEN Film Substrate
- Asahi Kasei Thermofil P-40TC-1156 40% Talc Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved