- EPICHEM Epiter PBT GF 30 Polybutylene Terephthalate, 30% Glass
EPICHEM Epiter PBT GF 30 Polybutylene Terephthalate, 30% Glass
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | Epiter |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epiter PBT GF 30 Polybutylene Terephthalate, 30% Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: 30% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0025 - 0.015 cm/cm | 0.0025 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638, ISO R527 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638, ISO R527 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 140 °C | 284 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 160 °C | 320 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 220 °C @Load 0.999 kg |
428 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.8 @Frequency 1000 Hz |
3.8 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz |
0.0020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 400 V | 400 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 3012 RC Polypropylene
- MV Labs LA900 LaPO4·xH2O Lanthanum phosphate hydrate
- Plastcom SLOVALEN PH 69 GF 25 Polypropylene Homopolymer, 25% Glass Fiber
- Kazanorgsintez Aluminum Hydroxychloride
- Trelleborg Fillite® 300W Alumino-silicate Cenospheres
- Ecomass® 1005ZD96 Tungsten Powder Filled Co-Polyamide, Injection Molding Grade
- ExxonMobil HDPE HD 6719.17 High Density Polyethylene Copolymer Resin
- Constellium ALPLAN® 5083 Rolled Precision Aluminum Plate, Milled Both Sides
- Arlon 55946C030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Asahi Glass Fluon® XAD912 PTFE Aqueous Dispersion
Copyright © lookpolymers.com All Rights Reserved