EMS-Grivory Grivory® TSG-15/4 PA666-GF15
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSG-15/4 PA666-GF15.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | ISO 62 |
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | conditioned; ISO 2039-1 |
| 160 MPa | 23200 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | conditioned; ISO 527-1/-2 |
| 120 MPa | 17400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 5.0 % | 5.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | conditioned; ISO 527-1/-2 |
| 6.00 GPa | 870 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eU |
| 6.00 J/cm² | 28.6 ft-lb/in² | conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | dry; ISO 179/1eA |
| 1.10 J/cm² | 5.23 ft-lb/in² | conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Electrical equipment | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HFD1014 PC Copolymer (Europe-Africa-Middle East)
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 61 Shore A (discontinued **)
- Hexion Bakelite™ PF 85 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Techmer ES Elastoblend® PA6/6 IM L UV Nylon 66
- DuPont Elvaloy® 1820 AC Ethylene and 20% Methyl Acrylate Copolymer
- Vista Metals Duramold-2™ Cast Aluminum Mold Plate
- 3M Controltac™ RG180-10 Graphic Film
- Overview of materials for Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
- Asahi Kasei Xyron® A0501 PPE/PA
Copyright © lookpolymers.com All Rights Reserved