Henkel Hysol EA 956 Paste Adhesive System
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Henkel |
| Trade Name | Hysol |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Henkel Hysol EA 956 Paste Adhesive System.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very low viscosity, cures at room temperatureDesigned for wet lay-up repairApplications: Structural Repair Low Viscosity Wet Lay-Up
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Storage Temperature | 4.00 °C | 39.2 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 40.0 MPa | 5800 psi | |
| Elongation at Break | 2.5 % | 2.5 % | |
| Tensile Modulus | 2.25 GPa | 326 ksi | |
| Compressive Strength | 116.6 MPa | 16910 psi | |
| Compressive Modulus | 4.00 GPa | 580 ksi | |
| Adhesive Bond Strength | 10.3 MPa @Temperature 93.0 °C |
1490 psi @Temperature 199 °F |
Tensile Lap Shear |
| 12.4 MPa @Temperature -55.0 °C |
1800 psi @Temperature -67.0 °F |
Tensile Lap Shear | |
| 15.9 MPa @Temperature 25.0 °C |
2310 psi @Temperature 77.0 °F |
Tensile Lap Shear |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 149 °C | 300 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 93.0 °C |
1.00 hour @Temperature 199 °F |
|
| 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
||
| Pot Life | 30 min | 30 min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Consistency | Low Viscosity | |
| Form | 2 parts | |
| Mix Ratio, Part A:Part B | 100:58 | |
| Peel Strength | Nil |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 GF 25 002 PA6 reinforced with glass fiber
- PTS Tristar® PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release
- PolyOne Geon™ Vinyl Flexible H43356A Polyvinyl Chloride, Flexible (PVC, Flexible)
- LyondellBasell Lupolen® 2425 K LDPE, Film Grade
- Global PP-1100-NK Polypropylene Homopolymer
- Materion Beryllium Copper Alloy 25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Borealis Borstar® MB7541 High Density Polyethylene for Injection Molding
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- Arlon 41570R015 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier
Copyright © lookpolymers.com All Rights Reserved