E-Polymers TEKAMID® TA210 LW TA210LW, Low Wear, Low Friction PA66, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TA210 LW TA210LW, Low Wear, Low Friction PA66, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low wear, Low frictionInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced
- Lord Adhesives Aeroglaze® 9953 Epoxy Primer Thinner
- Lehmann & Voss LUVOCOM® 1-0866 Polyamide 66, with aramid reinforcement, heat stabilized
- Stir SpA AF 95 (PVC)
- A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N774 Filler
- Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
- Clariant PA213M40 Nylon 6, 40% Mineral Reinforced, Heat Stabilized
- Arlon 56586R026 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics LNP Thermocomp MF0069S PP
Copyright © lookpolymers.com All Rights Reserved