- PolyOne Edgetek® AM-30GM/15TF Polyphthalamide (PPA), Glass Filled, PTFE Lubricated (discontinued **)
PolyOne Edgetek® AM-30GM/15TF Polyphthalamide (PPA), Glass Filled, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-30GM/15TF Polyphthalamide (PPA), Glass Filled, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.21 % | 0.21 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0065 cm/cm | 0.0060 - 0.0065 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.800 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 277 °C | 530 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 510 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Qualchem Danamid FGF-20 Polyamide 6, 20% Glass Fiber
- Chevron Phillips Vytek™ V205A Enhanced LLDPE Blown Film Resin (discontinued **)
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 7% Plasticizer (discontinued **)
- Huntsman AroCy M-10 Monomeric Bisphenol F Dicyanate
- Lubriplate Bar & Chain Oil Specialty Oil and Fluid
- SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI
- SABIC Innovative Plastics Ultem CRS5211 PEI (Asia Pacific)
- Carpenter Micro-Melt® 9 Annealed Tool Steel
- LG Chemical 15NFI GPPS
Copyright © lookpolymers.com All Rights Reserved