E-Polymers TEKAMID® JN2 PPE+PA66 Un-reinforced Chemical resistance PA/PPE Alloy

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO
Manufacturer	E-Polymers Co. Ltd.
Trade Name	TEKAMID®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers TEKAMID® JN2 PPE+PA66 Un-reinforced Chemical resistance PA/PPE Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/PPE alloy (Unreinforced, GF reinforced, MF reinforced)Information Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.13 g/cc	1.13 g/cc	ASTM D792
Water Absorption	0.50 % @Time 86400 sec	0.50 % @Time 24.0 hour
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	66.708 MPa	9675.2 psi	ASTM D638
Elongation at Break	50 %	50 %	ASTM D638
Flexural Strength	99.08 MPa	14370 psi	ASTM D790
Flexural Modulus	2.374 GPa	344.3 ksi	ASTM D790
Izod Impact, Notched	1.67 J/cm	3.12 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	204 °C	399 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	125 °C	257 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F