DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Glass Reinforced Polyamide 66Zytel 70G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
DAM; ISO 1183
Water Absorption 5.7 %

@Thickness 2.00 mm
 5.7 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.80 %

@Thickness 2.00 mm
 1.80 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 1.2 %
1.2 %
DAM; Immersion 24h; ASTM D570
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
50%RH; ISO 527-1/-2
200 MPa
29000 psi
DAM; ISO 527-1/-2
Tensile Stress 10.0 MPa

@Strain 0.120 %,
Time 3600 sec
 1450 psi

@Strain 0.120 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.125 %,
Time 36000 sec
 1450 psi

@Strain 0.125 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.130 %,
Time 360000 sec
 1450 psi

@Strain 0.130 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.150 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.150 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
DAM; ISO 527-1/-2
5.0 %
5.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
50%RH; ISO 527-1/-2
10.5 GPa
1520 ksi
DAM; ISO 527-1/-2
Flexural Strength 200 MPa
29000 psi
50%RH; ISO 178
290 MPa
42100 psi
DAM; ISO 178
Flexural Modulus 6.21 GPa
901 ksi
50%RH; ISO 178
9.30 GPa
1350 ksi
DAM; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
DAM; ISO 180/1A
15.0 kJ/m²
7.14 ft-lb/in²
50%RH; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1A
10.0 kJ/m²

@Temperature -40.0 °C
 4.76 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
10.0 kJ/m²

@Temperature -40.0 °C
 4.76 ft-lb/in²

@Temperature -40.0 °F
 50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
DAM; ISO 180/1U
90.0 kJ/m²
42.8 ft-lb/in²
50%RH; ISO 180/1U
70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1U
70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1U
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
DAM; ISO 179/1eU
10.0 J/cm²
47.6 ft-lb/in²
50%RH; ISO 179/1eU
7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
DAM; ISO 179/1eA
1.70 J/cm²
8.09 ft-lb/in²
50%RH; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
1.00 J/cm²

@Temperature -40.0 °C
 4.76 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
1.00 J/cm²

@Temperature -40.0 °C
 4.76 ft-lb/in²

@Temperature -40.0 °F
 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 3190 MPa

@Pressure 30.0 MPa,
Temperature 150 °C
 463000 psi

@Pressure 4350 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3210 MPa

@Pressure 25.0 MPa,
Temperature 150 °C
 466000 psi

@Pressure 3630 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3240 MPa

@Pressure 20.0 MPa,
Temperature 150 °C
 469000 psi

@Pressure 2900 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3260 MPa

@Pressure 15.0 MPa,
Temperature 150 °C
 473000 psi

@Pressure 2180 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3280 MPa

@Pressure 10.0 MPa,
Temperature 150 °C
 476000 psi

@Pressure 1450 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3290 MPa

@Pressure 5.00 MPa,
Temperature 150 °C
 478000 psi

@Pressure 725 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 5.00 MPa,
Temperature 100 °C
 518000 psi

@Pressure 725 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 10.0 MPa,
Temperature 100 °C
 518000 psi

@Pressure 1450 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 15.0 MPa,
Temperature 100 °C
 518000 psi

@Pressure 2180 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 20.0 MPa,
Temperature 100 °C
 518000 psi

@Pressure 2900 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 25.0 MPa,
Temperature 100 °C
 518000 psi

@Pressure 3630 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3570 MPa

@Pressure 30.0 MPa,
Temperature 100 °C
 518000 psi

@Pressure 4350 psi,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
8110 MPa

@Pressure 30.0 MPa,
Temperature 23.0 °C
 1.18e+6 psi

@Pressure 4350 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8150 MPa

@Pressure 25.0 MPa,
Temperature 23.0 °C
 1.18e+6 psi

@Pressure 3630 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8210 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 1.19e+6 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8270 MPa

@Pressure 15.0 MPa,
Temperature 23.0 °C
 1.20e+6 psi

@Pressure 2180 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8330 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 1.21e+6 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8380 MPa

@Pressure 5.00 MPa,
Temperature 23.0 °C
 1.21e+6 psi

@Pressure 725 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
8000 MPa

@Time 3600 sec
 1.16e+6 psi

@Time 1.00 hour
 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours 2680 MPa

@Pressure 30.0 MPa,
Temperature 150 °C
 388000 psi

@Pressure 4350 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
2690 MPa

@Pressure 25.0 MPa,
Temperature 150 °C
 391000 psi

@Pressure 3630 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
2710 MPa

@Pressure 20.0 MPa,
Temperature 150 °C
 393000 psi

@Pressure 2900 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
2730 MPa

@Pressure 15.0 MPa,
Temperature 150 °C
 396000 psi

@Pressure 2180 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
2740 MPa

@Pressure 10.0 MPa,
Temperature 150 °C
 398000 psi

@Pressure 1450 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
2750 MPa

@Pressure 5.00 MPa,
Temperature 150 °C
 399000 psi

@Pressure 725 psi,
Temperature 302 °F
 50%RH; ISO 11403-1 -2