DuPont Performance Polymers Zytel® 135F NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 135F NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Unreinforced Nucleated Polyamide 66 Zytel 135F NC010 is a nucleated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Water Absorption 8.5 %

@Thickness 2.00 mm
 8.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.70 %

@Thickness 2.00 mm
 2.70 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 64000 cP

@Shear Rate 5000 1/s,
Temperature 315 °C
 64000 cP

@Shear Rate 5000 1/s,
Temperature 599 °F
 ISO 11403-1 -2
83000 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 83000 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
105000 cP

@Shear Rate 5000 1/s,
Temperature 275 °C
 105000 cP

@Shear Rate 5000 1/s,
Temperature 527 °F
 ISO 11403-1 -2
134000 cP

@Shear Rate 500 1/s,
Temperature 315 °C
 134000 cP

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
195000 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 195000 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
284000 cP

@Shear Rate 500 1/s,
Temperature 275 °C
 284000 cP

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell M 64
64
50%RH; ISO 2039-2
87
87
DAM; ISO 2039-2
Hardness, Rockwell R 116
116
50%RH; ISO 2039-2
123
123
DAM; ISO 2039-2
Tensile Stress 7.47 MPa

@Strain 0.960 %,
Temperature 90.0 °C
 1080 psi

@Strain 0.960 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
11.4 MPa

@Strain 0.480 %,
Temperature 40.0 °C
 1650 psi

@Strain 0.480 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
17.8 MPa

@Strain 2.40 %,
Temperature 90.0 °C
 2580 psi

@Strain 2.40 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.0 MPa

@Strain 0.480 %,
Temperature 23.0 °C
 2610 psi

@Strain 0.480 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
22.8 MPa

@Strain 0.550 %,
Temperature 0.000 °C
 3310 psi

@Strain 0.550 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
24.5 MPa

@Strain 3.84 %,
Temperature 90.0 °C
 3550 psi

@Strain 3.84 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
26.5 MPa

@Strain 0.630 %,
Temperature -20.0 °C
 3840 psi

@Strain 0.630 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
41.6 MPa

@Strain 1.92 %,
Temperature 40.0 °C
 6030 psi

@Strain 1.92 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
60.5 MPa

@Strain 3.36 %,
Temperature 40.0 °C
 8770 psi

@Strain 3.36 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
65.5 MPa

@Strain 1.92 %,
Temperature 23.0 °C
 9500 psi

@Strain 1.92 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
65.7 MPa

@Strain 4.80 %,
Temperature 40.0 °C
 9530 psi

@Strain 4.80 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
82.7 MPa

@Strain 2.20 %,
Temperature 0.000 °C
 12000 psi

@Strain 2.20 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
92.9 MPa

@Strain 3.36 %,
Temperature 23.0 °C
 13500 psi

@Strain 3.36 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
95.4 MPa

@Strain 2.52 %,
Temperature -20.0 °C
 13800 psi

@Strain 2.52 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
117 MPa

@Strain 3.85 %,
Temperature 0.000 °C
 17000 psi

@Strain 3.85 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
133 MPa

@Strain 4.41 %,
Temperature -20.0 °C
 19300 psi

@Strain 4.41 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
3.00 MPa

@Strain 0.165 %,
Time 36000 sec
 435 psi

@Strain 0.165 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.192 %,
Time 360000 sec
 435 psi

@Strain 0.192 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.231 %,
Time 3.60e+6 sec
 435 psi

@Strain 0.231 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.146 %,
Time 3600 sec
 435 psi

@Strain 0.146 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.297 %,
Time 3.60e+7 sec
 435 psi

@Strain 0.297 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.45 %,
Time 3.60e+7 sec
 1740 psi

@Strain 1.45 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.656 %,
Time 3600 sec
 1740 psi

@Strain 0.656 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.18 %,
Time 3.60e+6 sec
 1740 psi

@Strain 1.18 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.947 %,
Time 360000 sec
 1740 psi

@Strain 0.947 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.772 %,
Time 36000 sec
 1740 psi

@Strain 0.772 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
Tensile Strength, Yield 67.0 MPa
9720 psi
50%RH; ISO 527-1/-2
96.0 MPa
13900 psi
DAM; ISO 527-1/-2
Elongation at Break 13 %
13 %
DAM; Nominal; ISO 527-1/-2
50 %
50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 4.5 %
4.5 %
DAM; ISO 527-1/-2
4.5 %
4.5 %
DAM; ISO 527-3
18 %
18 %
50%RH; ISO 527-1/-2
Tensile Modulus 2.00 GPa
290 ksi
50%RH; ISO 527-1/-2
3.60 GPa
522 ksi
DAM; ISO 527-1/-2
Shear Modulus 0.175 GPa

@Temperature 160 °C
 25.4 ksi

@Temperature 320 °F
 DAM; Dynamic; ISO 11403-1 -2
0.214 GPa

@Temperature 120 °C
 31.0 ksi

@Temperature 248 °F
 DAM; Dynamic; ISO 11403-1 -2
0.449 GPa

@Temperature 70.0 °C
 65.1 ksi

@Temperature 158 °F
 DAM; Dynamic; ISO 11403-1 -2
1.0685 GPa

@Temperature 20.0 °C
 154.98 ksi

@Temperature 68.0 °F
 DAM; Dynamic; ISO 11403-1 -2
1.171 GPa

@Temperature -20.0 °C
 169.8 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
1.259 GPa

@Temperature -50.0 °C
 182.6 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2
Shear Strength 0.0670 MPa

@Shear Rate 500 1/s,
Temperature 315 °C
 9.72 psi

@Shear Rate 500 1/s,
Temperature 599 °F
 ISO 11403-1 -2
0.0975 MPa

@Shear Rate 500 1/s,
Temperature 295 °C
 14.1 psi

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
0.142 MPa

@Shear Rate 500 1/s,
Temperature 275 °C
 20.6 psi

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Secant Modulus 1.66 GPa

@Strain 3.84 %,
Temperature 40.0 °C
 240 ksi

@Strain 3.84 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
2.17 GPa

@Strain 1.92 %,
Temperature 40.0 °C
 314 ksi

@Strain 1.92 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
2.375 GPa

@Strain 0.480 %,
Temperature 40.0 °C
 344.5 ksi

@Strain 0.480 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
2.52 GPa

@Strain 3.84 %,
Temperature 23.0 °C
 365 ksi

@Strain 3.84 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
2.7381 GPa

@Strain 5.04 %,
Temperature -20.0 °C
 397.13 ksi

@Strain 5.04 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
2.77 GPa

@Strain 4.40 %,
Temperature 0.000 °C
 402 ksi

@Strain 4.40 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
3.41 GPa

@Strain 1.92 %,
Temperature 23.0 °C
 495 ksi

@Strain 1.92 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2