SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Asia Pacific)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.970 % | 0.970 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.030 cm/cm @Time 86400 sec |
0.025 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.025 - 0.027 cm/cm @Time 86400 sec |
0.025 - 0.027 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 53.0 MPa | 7690 psi | ISO 527 | |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Tensile Modulus | 2.65 GPa | 384 ksi | 50 mm/min; ASTM D638 |
| 3.05 GPa | 442 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| 2.26 GPa | 328 ksi | ISO 178 | |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.67 J/cm | 25.61 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 85.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS (Asia Pacific)
- Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy
- Solvay GERONOL® AG 900 Surfactant
- Cossa Polimeri ESTACARB 1560 V0 HF Flame Retardant Polycarbonate
- ELASTO UK Dryflex® 660700S SEBS Based Material, Semi-Filled Qualities, 70A Hardness, Natural
- Crucible Steel CPM® Rex® T15(HS), AISI T15 High Speed Steel Rex® T15(HS)
- DuPont Performance Polymers Crastin® S600LF NC010 PBT
- Chosun Refractories L12H Magnesia Carbon Bricks for Ladle Slag Line
- Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F)
Copyright © lookpolymers.com All Rights Reserved