NOVA Chemicals Sclair® 13J7 Octene LMDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 13J7 Octene LMDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, high clarity.Applications: Film.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.95 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Elongation at Break, MD | 744 % | 744 % | ASTM D882 |
| Film Elongation at Break, TD | 980 % | 980 % | ASTM D882 |
| Secant Modulus, MD | 0.380 GPa | 55.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.450 GPa | 65.3 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.00 g/micron | 76.2 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Dart Drop | 4.00 g/micron | 102 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.0 MPa | 6380 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.9 % @Thickness 0.0250 mm |
8.9 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Momentive Performance Materials AC6001 Boron Nitride (BN) Powder
- SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East)
- Hexcel® HexForce™ GA030 Carbon Fabric
- Tipco Tipcolene® SEB 300 FR - UL94-V-0 Flame Retardant, 10% Chemically Coupled Glass Fiber Polypropylene Homopolymer
- ExxonMobil Escorene™ UL 40028CC Ethylene Vinyl Acetate Copolymer (European Grade)
- Braskem LH0820/30AF Blown Film Extrusion Linear Low Density Polyethylene
- C.O.I.M. PLAXTER® P 20 Polymeric Plasticizer
- ATI Wah Chang Zircadyne® Alloy Zr 705
- ExxonMobil SAE 30 Mobilgard M40 Series
Copyright © lookpolymers.com All Rights Reserved