DuPont Performance Polymers Rynite® FR530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Flame Retardant Polyethylene Terephthalate Rynite FR530 NC010 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Water Absorption 0.75 %

@Thickness 2.00 mm
0.75 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.150 %

@Thickness 2.00 mm
0.150 %

@Thickness 0.0787 in
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 135 MPa
19600 psi
ISO 527-1/-2
Tensile Stress 16.0 MPa

@Strain 0.450 %,
Temperature 150 °C
2320 psi

@Strain 0.450 %,
Temperature 302 °F
ISO 11403-1 -2
20.1 MPa

@Strain 0.380 %,
Temperature 90.0 °C
2920 psi

@Strain 0.380 %,
Temperature 194 °F
ISO 11403-1 -2
21.1 MPa

@Strain 0.210 %,
Temperature 40.0 °C
3060 psi

@Strain 0.210 %,
Temperature 104 °F
ISO 11403-1 -2
22.0 MPa

@Strain 0.180 %,
Temperature 0.000 °C
3190 psi

@Strain 0.180 %,
Temperature 32.0 °F
ISO 11403-1 -2
22.7 MPa

@Strain 0.200 %,
Temperature 23.0 °C
3290 psi

@Strain 0.200 %,
Temperature 73.4 °F
ISO 11403-1 -2
24.3 MPa

@Strain 0.180 %,
Temperature -40.0 °C
3520 psi

@Strain 0.180 %,
Temperature -40.0 °F
ISO 11403-1 -2
42.0 MPa

@Strain 1.80 %,
Temperature 150 °C
6090 psi

@Strain 1.80 %,
Temperature 302 °F
ISO 11403-1 -2
50.0 MPa

@Strain 3.16 %,
Temperature 150 °C
7250 psi

@Strain 3.16 %,
Temperature 302 °F
ISO 11403-1 -2
53.0 MPa

@Strain 4.51 %,
Temperature 150 °C
7690 psi

@Strain 4.51 %,
Temperature 302 °F
ISO 11403-1 -2
54.1 MPa

@Strain 1.50 %,
Temperature 90.0 °C
7850 psi

@Strain 1.50 %,
Temperature 194 °F
ISO 11403-1 -2
67.3 MPa

@Strain 2.61 %,
Temperature 90.0 °C
9760 psi

@Strain 2.61 %,
Temperature 194 °F
ISO 11403-1 -2
70.9 MPa

@Strain 3.72 %,
Temperature 90.0 °C
10300 psi

@Strain 3.72 %,
Temperature 194 °F
ISO 11403-1 -2
72.3 MPa

@Strain 0.840 %,
Temperature 40.0 °C
10500 psi

@Strain 0.840 %,
Temperature 104 °F
ISO 11403-1 -2
76.3 MPa

@Strain 0.770 %,
Temperature 23.0 °C
11100 psi

@Strain 0.770 %,
Temperature 73.4 °F
ISO 11403-1 -2
81.0 MPa

@Strain 0.740 %,
Temperature 0.000 °C
11700 psi

@Strain 0.740 %,
Temperature 32.0 °F
ISO 11403-1 -2
84.9 MPa

@Strain 0.700 %,
Temperature -40.0 °C
12300 psi

@Strain 0.700 %,
Temperature -40.0 °F
ISO 11403-1 -2
105 MPa

@Strain 1.47 %,
Temperature 40.0 °C
15200 psi

@Strain 1.47 %,
Temperature 104 °F
ISO 11403-1 -2
113 MPa

@Strain 1.34 %,
Temperature 23.0 °C
16400 psi

@Strain 1.34 %,
Temperature 73.4 °F
ISO 11403-1 -2
120 MPa

@Strain 2.12 %,
Temperature 40.0 °C
17400 psi

@Strain 2.12 %,
Temperature 104 °F
ISO 11403-1 -2
124 MPa

@Strain 1.29 %,
Temperature 0.000 °C
18000 psi

@Strain 1.29 %,
Temperature 32.0 °F
ISO 11403-1 -2
134 MPa

@Strain 1.90 %,
Temperature 23.0 °C
19400 psi

@Strain 1.90 %,
Temperature 73.4 °F
ISO 11403-1 -2
137 MPa

@Strain 1.23 %,
Temperature -40.0 °C
19900 psi

@Strain 1.23 %,
Temperature -40.0 °F
ISO 11403-1 -2
153 MPa

@Strain 1.85 %,
Temperature 0.000 °C
22200 psi

@Strain 1.85 %,
Temperature 32.0 °F
ISO 11403-1 -2
176 MPa

@Strain 1.75 %,
Temperature -40.0 °C
25500 psi

@Strain 1.75 %,
Temperature -40.0 °F
ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527-1/-2
Flexural Modulus 10.5 GPa
1520 ksi
ISO 178
Secant Modulus 6.61 GPa

@Strain 1.68 %,
Temperature 40.0 °C
958 ksi

@Strain 1.68 %,
Temperature 104 °F
ISO 11403-1 -2
7.9085 GPa

@Strain 1.53 %,
Temperature 23.0 °C
1147.0 ksi

@Strain 1.53 %,
Temperature 73.4 °F
ISO 11403-1 -2
8.61 GPa

@Strain 0.840 %,
Temperature 40.0 °C
1250 ksi

@Strain 0.840 %,
Temperature 104 °F
ISO 11403-1 -2
9.19 GPa

@Strain 1.48 %,
Temperature 0.000 °C
1330 ksi

@Strain 1.48 %,
Temperature 32.0 °F
ISO 11403-1 -2
9.91 GPa

@Strain 0.770 %,
Temperature 23.0 °C
1440 ksi

@Strain 0.770 %,
Temperature 73.4 °F
ISO 11403-1 -2
10.0 GPa

@Strain 0.210 %,
Temperature 40.0 °C
1460 ksi

@Strain 0.210 %,
Temperature 104 °F
ISO 11403-1 -2
10.8 GPa

@Strain 1.40 %,
Temperature -40.0 °C
1560 ksi

@Strain 1.40 %,
Temperature -40.0 °F
ISO 11403-1 -2
10.9 GPa

@Strain 0.740 %,
Temperature 0.000 °C
1590 ksi

@Strain 0.740 %,
Temperature 32.0 °F
ISO 11403-1 -2
11.35 GPa

@Strain 0.200 %,
Temperature 23.0 °C
1646 ksi

@Strain 0.200 %,
Temperature 73.4 °F
ISO 11403-1 -2
12.1 GPa

@Strain 0.700 %,
Temperature -40.0 °C
1760 ksi

@Strain 0.700 %,
Temperature -40.0 °F
ISO 11403-1 -2
12.2 GPa

@Strain 0.180 %,
Temperature 0.000 °C
1770 ksi

@Strain 0.180 %,
Temperature 32.0 °F
ISO 11403-1 -2
13.5 GPa

@Strain 0.180 %,
Temperature -40.0 °C
1960 ksi

@Strain 0.180 %,
Temperature -40.0 °F
ISO 11403-1 -2
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 11200 MPa

@Time 3600 sec
1.62e+6 psi

@Time 1.00 hour
ISO 899-1
Tensile Creep Modulus, 1000 hours 9700 MPa

@Time 3.60e+6 sec
1.41e+6 psi

@Time 1000 hour
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C
10.6 µin/in-°F
ISO 11359-1/-2
22.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
12.2 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM D150
3.8

@Frequency 1000 Hz
3.8

@Frequency 1000 Hz
ASTM D150
4.7

@Frequency 1.00e+6 Hz
4.7

@Frequency 1.00e+6 Hz
IEC 60250
4.8

@Frequency 100 Hz
4.8

@Frequency 100 Hz
IEC 60250
Dielectric Strength 33.0 kV/mm
838 kV/in
IEC 60243-1
Dissipation Factor 0.0070

@Frequency 100 Hz
0.0070

@Frequency 100 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
0.011

@Frequency 1000 Hz
0.011

@Frequency 1000 Hz
ASTM D150
0.018

@Frequency 1.00e+6 Hz
0.018

@Frequency 1.00e+6 Hz
ASTM D150
Comparative Tracking Index 200 V
200 V
IEC 60112
250 - 400 V
250 - 400 V
UL 746A