DuPont Performance Polymers Minlon® 10B40HS1 BK061 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Minlon® 10B40HS1 BK061 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Minlon® 10B40HS1 BK061 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | DAM; ASTM D792 |
| Density | 1.51 g/cc | 0.0546 lb/in³ | DAM; ISO 1183 |
| Filler Content | 40 % | 40 % | DAM |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 1.60 mm |
0.0040 in/in @Thickness 0.0630 in |
Flow; DAM |
| 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
Flow; DAM | |
| 0.0060 cm/cm @Thickness 6.40 mm |
0.0060 in/in @Thickness 0.252 in |
Flow; DAM | |
| 0.0090 cm/cm @Thickness 1.60 mm |
0.0090 in/in @Thickness 0.0630 in |
Transverse; DAM | |
| 0.0090 cm/cm @Thickness 3.20 mm |
0.0090 in/in @Thickness 0.126 in |
Transverse; DAM | |
| 0.011 cm/cm @Thickness 6.40 mm |
0.011 in/in @Thickness 0.252 in |
Transverse; DAM | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa @Temperature 23.0 °C |
13800 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| Tensile Strength | 87.0 MPa @Temperature 23.0 °C |
12600 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Elongation at Break | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
DAM; ASTM D638 | |
| Tensile Modulus | 10.0 GPa @Temperature 23.0 °C |
1450 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
| Flexural Strength | 148 MPa @Temperature 23.0 °C |
21500 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
| Flexural Modulus | 8.62 GPa @Temperature 23.0 °C |
1250 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
| 9.50 GPa @Temperature 23.0 °C |
1380 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.599 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm @Temperature 23.0 °C |
5.99 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² @Temperature -40.0 °C |
1.19 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 3.50 kJ/m² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -40.0 °C |
0.952 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
29.4 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
| 53.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
29.4 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 | |
| 66.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.7 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 66.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.7 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 110 µm/m-°C @Temperature 55.0 - 160 °C |
61.1 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| 110 µm/m-°C @Temperature 55.0 - 160 °C |
61.1 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 263 °C | 505 °F | DAM; ASTM D3418 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| 210 °C | 410 °F | DAM; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 °C | 563 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | DAM |
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Features | Warpage, Low | DAM |
| Filler | Mineral filler | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66-MD40< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| Resin Identification | PA66-MD40 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| Uses | Appliance Components | DAM |
| Automotive Applications | DAM | |
| Gears | DAM | |
| Industrial Applications | DAM | |
| Parts, Engineering | DAM |
Users viewing this material also viewed the following:
- North Wood Plastics HDPE with 40% Wood Fiber
- SABIC Innovative Plastics Lexan® LR180R PC (Europe-Africa-Middle East)
- Nilit FRIANYL B63 FK 2010 Nylon 6 for injection molding, 20% glass fiber and 10% glass ball reinforced
- Kaneka PHBH Semi-Rigid Bio-based Polymer
- ExxonMobil 680 Mobilgear SHC Series
- Dow PAPI™ 95 Polymeric MDI
- 3M 9018FL Screen Printable Sheet Polyester Label Material
- SABIC Innovative Plastics LNP VERTON UX06451 PPA (Europe-Africa-Middle East)
- DuPont Performance Polymers Zytel® 70G25HSL NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved