DuPont Performance Polymers Delrin® 500TL NC010 Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 500TL NC010 Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500TL is a medium viscosity acetal homopolymer resin containing 1.5% Teflon PTFE Micropowder. It is designed for applications requiring moderate low wear and fInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Water Absorption	0.90 % @Thickness 2.00 mm	0.90 % @Thickness 0.0787 in	Sim. to ISO 62
Moisture Absorption	0.170 % @Thickness 2.00 mm	0.170 % @Thickness 0.0787 in	Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.018 cm/cm	0.018 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.017 cm/cm	0.017 in/in	ISO 294-4 2577
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133
	14 g/10 min @Load 2.16 kg, Temperature 190 °C	14 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Stress	31.8 MPa @Strain 1.10 %, Temperature 23.0 °C	4610 psi @Strain 1.10 %, Temperature 73.4 °F	ISO 11403-1 -2
	34.3 MPa @Strain 1.10 %, Temperature 0.000 °C	4970 psi @Strain 1.10 %, Temperature 32.0 °F	ISO 11403-1 -2
	36.6 MPa @Strain 0.900 %, Temperature -40.0 °C	5310 psi @Strain 0.900 %, Temperature -40.0 °F	ISO 11403-1 -2
	62.6 MPa @Strain 4.40 %, Temperature 23.0 °C	9080 psi @Strain 4.40 %, Temperature 73.4 °F	ISO 11403-1 -2
	66.6 MPa @Strain 7.70 %, Temperature 23.0 °C	9660 psi @Strain 7.70 %, Temperature 73.4 °F	ISO 11403-1 -2
	67.2 MPa @Strain 11.0 %, Temperature 23.0 °C	9750 psi @Strain 11.0 %, Temperature 73.4 °F	ISO 11403-1 -2
	71.7 MPa @Strain 4.30 %, Temperature 0.000 °C	10400 psi @Strain 4.30 %, Temperature 32.0 °F	ISO 11403-1 -2
	76.7 MPa @Strain 7.60 %, Temperature 0.000 °C	11100 psi @Strain 7.60 %, Temperature 32.0 °F	ISO 11403-1 -2
	77.5 MPa @Strain 10.8 %, Temperature 0.000 °C	11200 psi @Strain 10.8 %, Temperature 32.0 °F	ISO 11403-1 -2
	88.1 MPa @Strain 3.70 %, Temperature -40.0 °C	12800 psi @Strain 3.70 %, Temperature -40.0 °F	ISO 11403-1 -2
	96.6 MPa @Strain 6.50 %, Temperature -40.0 °C	14000 psi @Strain 6.50 %, Temperature -40.0 °F	ISO 11403-1 -2
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
Elongation at Break	20 %	20 %	Nominal; ISO 527-1/-2
Elongation at Yield	13 %	13 %	ISO 527-1/-2
Tensile Modulus	3.30 GPa	479 ksi	ISO 527-1/-2
Flexural Modulus	3.10 GPa	450 ksi	ISO 178
Secant Modulus	0.425 GPa @Strain 7.10 %, Temperature 100 °C	61.7 ksi @Strain 7.10 %, Temperature 212 °F	ISO 11403-1 -2
	0.532 GPa @Strain 7.50 %, Temperature 80.0 °C	77.2 ksi @Strain 7.50 %, Temperature 176 °F	ISO 11403-1 -2
	0.689 GPa @Strain 3.50 %, Temperature 100 °C	99.9 ksi @Strain 3.50 %, Temperature 212 °F	ISO 11403-1 -2
	0.760 GPa @Strain 8.80 %, Temperature 23.0 °C	110 ksi @Strain 8.80 %, Temperature 73.4 °F	ISO 11403-1 -2
	0.882 GPa @Strain 3.80 %, Temperature 80.0 °C	128 ksi @Strain 3.80 %, Temperature 176 °F	ISO 11403-1 -2
	0.897 GPa @Strain 8.60 %, Temperature 0.000 °C	130 ksi @Strain 8.60 %, Temperature 32.0 °F	ISO 11403-1 -2
	0.944 GPa @Strain 0.900 %, Temperature 100 °C	137 ksi @Strain 0.900 %, Temperature 212 °F	ISO 11403-1 -2
	1.31 GPa @Strain 7.40 %, Temperature -40.0 °C	190 ksi @Strain 7.40 %, Temperature -40.0 °F	ISO 11403-1 -2
	1.38 GPa @Strain 0.900 %, Temperature 80.0 °C	200 ksi @Strain 0.900 %, Temperature 176 °F	ISO 11403-1 -2
	1.42 GPa @Strain 4.40 %, Temperature 23.0 °C	206 ksi @Strain 4.40 %, Temperature 73.4 °F	ISO 11403-1 -2
	1.67 GPa @Strain 4.30 %, Temperature 0.000 °C	242 ksi @Strain 4.30 %, Temperature 32.0 °F	ISO 11403-1 -2
	2.38 GPa @Strain 3.70 %, Temperature -40.0 °C	345 ksi @Strain 3.70 %, Temperature -40.0 °F	ISO 11403-1 -2
	2.89 GPa @Strain 1.10 %, Temperature 23.0 °C	419 ksi @Strain 1.10 %, Temperature 73.4 °F	ISO 11403-1 -2
	3.12 GPa @Strain 1.10 %, Temperature 0.000 °C	452 ksi @Strain 1.10 %, Temperature 32.0 °F	ISO 11403-1 -2
	4.07 GPa @Strain 0.900 %, Temperature -40.0 °C	590 ksi @Strain 0.900 %, Temperature -40.0 °F	ISO 11403-1 -2
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180/1A
	6.00 kJ/m² @Temperature -40.0 °C	2.86 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
Charpy Impact Unnotched	17.0 J/cm²	80.9 ft-lb/in²	ISO 179/1eU
	16.0 J/cm² @Temperature -30.0 °C	76.1 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179/1eA
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	103 °C	217 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Dielectric Constant	3.6 @Frequency 100 Hz	3.6 @Frequency 100 Hz	IEC 60250
	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Descriptive Properties	Value	Comments
Additives	Lubricants
	Release agent
Delivery Form	Pellets
Part Marking Code	>POM-SD<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-SD	ISO 1043