PolyOne Edgetek® AM 33 GF/000 L HS Black Polyphthalamide (PPA), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM 33 GF/000 L HS Black Polyphthalamide (PPA), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Heat StabilizedBlackEnhanced LubricationGlass Fiber ReinforcedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 - 0.0040 cm/cm | 0.0035 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 217 MPa | 31500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 12.4 GPa | 1800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 299 °C | 570 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 288 °C | 550 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 110 - 121 °C | 230 - 250 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPE-2272ALC PVC
- Plastcom SLOVASTER® B GF 30 FRL 4 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant
- Polimeri Europa Eraclene® MQ 70 U High Density Polyethylene - Injection Molding
- PolyOne Geon™ Vinyl Flexible R5145A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lehmann & Voss LUVOCOM® 1301-7661/RD PPS, linear, with glass fiber and PTFE
- Styrolution PS 3100/3101 GPPS
- Daikin NEOFLON NF-0500 FEP Film
- ExxonMobil Mobilarma 525
- 3M 500 Impact Stripping Tape
- Eastman E6838-975F Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved