DuPont Bexloy® AXW507NC010 Modified Ionomer Resin (discontinued **)
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | DuPont Bexloy® AXW507NC010 Modified Ionomer Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A modified ionomer resin engineered for injection molded exterior automotive applications.Availability: North AmericaInformation provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 - ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 1.7 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C |
1.7 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 - ISO 527-2 |
| Elongation at Break | 400 % | 400 % | ASTM D638 - ISO 527-2 |
| Flexural Modulus | 0.68200 GPa | 98.916 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm <br>@Temperature -30.0 °C |
16.0 ft-lb/in <br>@Temperature -22.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J <br>@Temperature -30.0 °C |
26.7 ft-lb <br>@Temperature -22.0 °F |
ASTM D3029 |
| Impact Test | 18.0 J <br>@Temperature -30.0 °C |
13.2 ft-lb <br>@Temperature -22.0 °F |
Rheometric, 5mph, 1/2" diameter tup, 3" diameter ring |
| 21.9 J <br>@Temperature 22.8 °C |
16.2 ft-lb <br>@Temperature 73.0 °F |
Rheometric, 5mph, 1/2" diameter tup, 3" diameter ring | |
| Tear Strength | 164 kN/m | 935 pli | At 73°F; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 84.0 µm/m-°C <br>@Temperature -30.0 - 80.0 °C |
46.7 µin/in-°F <br>@Temperature -22.0 - 176 °F |
ASTM E831 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 238 - 271 °C | 460 - 520 °F | |
| Melt Temperature | 238 - 288 °C | 460 - 550 °F | |
| Mold Temperature | 15.6 - 60.0 °C | 60.0 - 140 °F | |
| Drying Temperature | 60.0 - 79.4 °C | 140 - 175 °F | |
| Moisture Content | <= 0.080 % | <= 0.080 % | |
| Back Pressure | >= 0.345 MPa | >= 50.0 psi | no units given |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Sag, 82°C | 13 mm | ASTM D3770 |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- PolyMirae Moplen RP343N Injection Molding Grade Polypropylene
- LG Chemical Lupoy 1200-03 Polycarbonate Resin
- Greene Tweed CHEMRAZ® 565 Perfluoroelastomer
- Techmer ES HiFill FR® PA6/6 GF30 FR BK 30% Glass Filled
- Spartech DP5120 Talc Filled Homopolymer
- SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear
- A. Schulman POLYBLAK™ 4692 Premium Black Color Concentrate, 35% Carbon Black Based In LLDPE
- ATI Allvac® 3-2.5 Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
- CeramTec Rubalit® A 1896 Alumina
Copyright © lookpolymers.com All Rights Reserved