Material Notes:

LNP STAT-KON* AE0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/inÂ³	ASTM D 792
	1.26 g/cc	0.0455 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	0.31 %	0.31 %	23Â°C / 50% RH; ISO 62
	0.30 % @Time 86400 sec	0.30 % @Time 24.0 hour	50% RH; ASTM D 570
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Time 86400 sec	0.0030 in/in @Time 24.0 hour	ASTM D 955
	0.0032 cm/cm @Time 86400 sec	0.0032 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0016 cm/cm @Time 86400 sec	0.0016 in/in @Time 24.0 hour	ISO 294
	0.0020 cm/cm @Time 86400 sec	0.0020 in/in @Time 24.0 hour	ASTM D 955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 MPa	9430 psi	ISO 527
	103 MPa	14900 psi	ASTM D 638
Elongation at Break	1.5 %	1.5 %	ASTM D 638
	2.3 %	2.3 %	ISO 527
Tensile Modulus	11.23 GPa	1629 ksi	50 mm/min; ASTM D 638
Flexural Strength	151 MPa	21900 psi	ASTM D 790
	164 MPa	23800 psi	ISO 178
Flexural Modulus	8.27 GPa	1200 ksi	ASTM D 790
	9.30 GPa	1350 ksi	ISO 178
Izod Impact, Notched	0.210 J/cm @Temperature 23.0 Â°C	0.393 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	1.48 J/cm @Temperature 23.0 Â°C	2.77 ft-lb/in @Temperature 73.4 Â°F	ASTM D 4812
Izod Impact, Notched (ISO)	4.00 kJ/mÂ² @Temperature 23.0 Â°C	1.90 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	17.0 kJ/mÂ² @Temperature 23.0 Â°C	8.09 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603
	6.00 J @Temperature 23.0 Â°C	4.43 ft-lb @Temperature 73.4 Â°F	Instrumented Impact Energy @ peak; ASTM D 3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	101 Â°C	214 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	101 Â°C @Thickness 3.20 mm	214 Â°F @Thickness 0.126 in	unannealed; ASTM D 648