- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Diamond Polymers ASA T-110
Diamond Polymers ASA T-110
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA T-110.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Medium Heat ResistanceInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.77 GPa | 257 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
5.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C | 183 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 98.9 °C | 210 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 120 °C | 248 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 229 - 260 °C | 445 - 500 °F | |
| Middle Barrel Temperature | 232 - 266 °C | 450 - 510 °F | |
| Front Barrel Temperature | 235 - 271 °C | 455 - 520 °F | |
| Nozzle Temperature | 221 - 271 °C | 430 - 520 °F | |
| Melt Temperature | 221 - 271 °C | 430 - 520 °F | Melt temperatures above 530°F are not recommended, and may result in color shifts and or thermal instability. |
| Mold Temperature | 37.8 - 82.2 °C | 100 - 180 °F | Higher mold temperature can aid flow in processing, provides a better surface finish, and creates less residual stress in the finished products. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Back Pressure | 0.517 - 1.03 MPa | 75.0 - 150 psi |
Users viewing this material also viewed the following:
- Oceanchem Group Potassium Formate 96-98% flakes/powder
- Premix Premi-Glas® 2203-25 CR-SX-HT Fiberglass Reinforced Thermoset SMC
- PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6
- Polimeri Europa Edistir RC 600 Polystyrene
- MetalTek Bearium® B-4 Bearing Bronze
- Techmer ES HiFill® PA6/6 GF43 HS L BK001 43% Glass Filled
- Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Tape Form
- EMS-Griltech Griltex® 1A Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- ExxonMobil Escorene™ UL 7521 Ethylene Vinyl Acetate Copolymer
- Carlson C 201 Commercially Pure Nickel
Copyright © lookpolymers.com All Rights Reserved