- SABIC Innovative Plastics LNP LUBRICOMP ML004 PP
SABIC Innovative Plastics LNP LUBRICOMP ML004 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ML004 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ML004 is a product based on Polypropylene containing 20% PTFE. Added features of this grade include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
| 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 10.4 % | 10.4 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 5.5 % | 5.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.62 GPa | 235 ksi | 1 mm/min; ISO 527 |
| 1.95 GPa | 283 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 1.59 GPa | 231 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.59 GPa | 231 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.16 J/cm | 7.79 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.89 | 0.89 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.70 | 0.70 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 220 x 10-8 mm³/N-M | 109 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 134 µm/m-°C @Temperature -30.0 - 30.0 °C |
74.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature -30.0 - 30.0 °C |
70.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 57.0 °C @Thickness 3.20 mm |
135 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 203 (SO) Synthetic Oil
- Park Electrochemical Nelco® NX9245 PTFE Laminate, Woven-Glass Reinforced
- Pinnacle Polymers 2135 Impact Polypropylene Copolymer, Injection Molding Grade
- LG Chemical LUCEL N109LDS POM, Chemical Resistance
- SABIC Innovative Plastics LNP THERMOCOMP PH0240A PA 6
- Solvay MACKSTAT® DM Surfactant
- Unifrax Fiberfrax® Round Braid
- E-Polymers TEKAMID® TA210HI , High Impact Resistance PA66, DAM
- Materion Beryllium Copper Alloy 3 Wire; H (TD04) Temper; 1.3-12.7 mm Diameter (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved