SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.270 % | 0.270 % | 50% RH, 24 hrs; ASTM D570 |
| 0.420 % | 0.420 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm @Time 86400 sec |
0.0027 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0123 cm/cm @Time 86400 sec |
0.0123 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 205 MPa | 29700 psi | ISO 527 |
| 236 MPa | 34200 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D638 | |
| Tensile Modulus | 14.34 GPa | 2080 ksi | 1 mm/min; ISO 527 |
| 16.13 GPa | 2339 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 311 MPa | 45100 psi | ASTM D790 |
| 321 MPa | 46600 psi | ISO 178 | |
| Flexural Modulus | 13.44 GPa | 1949 ksi | ASTM D790 |
| 13.8 GPa | 2000 ksi | ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.70 J/cm | 16.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 24.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 281 °C @Thickness 3.20 mm |
538 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lord Adhesives Thermosetâ„¢ LS 213-9 Unfilled Epoxy Encapsulant
- Jackon JACKOCELL® R212 Expanded Polystyrene Construction and Block Molding
- Johnson Matthey Copper-flo AWS Alloy for Fluxless Brazing of Copper
- Von Roll Isola IMI Varnish 74010A Epoxy Varnish for Electrical Insulation
- A. Schulman POLYFORT™ PP 1930UX Extra High Flow, UV Stabilized Copolymer Polypropylene
- Eagle Brass 762 Nickel Silver 12%, Extra Hard
- CoorsTek ZDY Yttria Fully Stabilized Zirconia
- BASF Capron® 8332G Impact Modified, 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved