- Diamond Polymers ABS 3501 GF-20
Diamond Polymers ABS 3501 GF-20
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3501 GF-20.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Reinforced Grade, 20%Glass FilledInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.80 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 67.6 MPa | 9800 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 4.43 GPa | 642 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 215 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| Vicat Softening Point | 113 °C | 236 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Oceanchem Group Triethyl Phosphate (TEP)
- Omni Plastics OmniLon™ 6/6 PA6/6 GR15 MF25 Glass/Mineral Filled Nylon
- Potters Industries Conduct-O-Fil® AgClad 12 Silver-coated Glass Fibers
- Solvay Specialty Polymers Halar® 5001C Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- SABIC Innovative Plastics Valox® VX3101N PBT (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-1140D BLK Thermoplastic Elastomer
- DuPont Teijin Films Melinex® 475 Polyester Film, 200 Gauge
- Carpenter HyMu "80"® Electronic Alloy, Cold Drawn Bar
- CEN® Electronic Material CN Polyimide Film, 6 Mil Thickness
Copyright © lookpolymers.com All Rights Reserved