DSM Stanyl® TE250F9 (DAM) Nylon 46 45% Glass Reinforced, Heat Stabilized, Flame Retardant (North America)
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Flame Retarded + Glass Fiber Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Stanyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Stanyl® TE250F9 (DAM) Nylon 46 45% Glass Reinforced, Heat Stabilized, Flame Retardant (North America).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DSM Engineering Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 50% RH / 23°C; Similar to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eU |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
UL746B |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
Users viewing this material also viewed the following:
- Kolon KOCETAL® WR301 Wear Modified Acetal Resin
- Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
- Shandong Dongyue Polymer DF-302 PTFE Aqueous Dispersion 60%
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- CENTROPLAST CENTROMID 12 Polyamide 12
- SABIC Innovative Plastics Lexan® LUX7630C PC COPOLYMER (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved