DSM Stanyl® SC50 PA46-GF30 FR
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Flame Retarded + Glass Fiber Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Stanyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Stanyl® SC50 PA46-GF30 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Flame Retardant, Halogen free and free of red phosphorous
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.10 % | 2.10 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | cond; ISO 527-1/-2 |
| 140 MPa | 20300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 1.7 % | 1.7 % | dry; ISO 527-1/-2 |
| 2.5 % | 2.5 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
| 12.5 GPa | 1810 ksi | dry; ISO 527-1/-2 | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | cond; ISO 178 |
| 12.5 GPa | 1810 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 425 V | 425 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AE-8133 Polyphthalamide (PPA) (discontinued **)
- Covestro Texin® 5286 Thermoplastic Polyurethane, Polyether-based, Medical (discontinued **)
- LG Chemical ALPHALAC SG910 HIPS
- Lubriplate 107 Calcium Type Multi-Purpose Grease
- CoorsTek Epoxy Seal 923 (ES-923) B-staged epoxy lids
- Fainplast Compounds FR 91 Flexible PVC, Insulation
- Eurotec® Tecomid® NA40 GR35 NL HS PA6.6, 35% glass fiber reinforced, heat stabilized, natural
- Aclo Accutech ABS ABS834G30L Glass Reinforced
- BASF Novolen® 2309 L Polypropylene
- Nye Lubricants UniFlor 8911R (891RP-1) (UF) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved