DuPont™ Kapton® 200HN Polyimide Film, 50 Micron Thickness

Category Polymer , Film , Thermoset , Polyimide, TS , Polyimide, Thermoset Film
Manufacturer DuPont
Trade Name Kapton®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Kapton® 200HN Polyimide Film, 50 Micron Thickness.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Available in thicknesses from 0.3 mil (7.5 µm) to 5 mil (125 µm).General Kapton® information: Kapton® is synthesized by polymerizing an aromatic dianhydride with an aromatic diamine. It has excellent chemical resistance; there are no known organic solvents for the film. It does not melt. It can be used at both high and low temperature extremes. Kapton® polyimide films can be used in a variety of electrical and electronic uses: wire and cable tapes, formed coil insulation, substrates for printed circuit boards, motor slot liners, magnet wire insulation, transformer and capacitor insulation, magnetic and pressure-sensitive tapes, and tubing.Data provided by DuPont High Performance Films.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Water Absorption 2.8 %
2.8 %
24 hr/23°C. ASTM D570
Moisture Absorption at Equilibrium 1.8 %
1.8 %
50% RH; 23°C
Water Vapor Transmission 3.50 g/m²/day
0.225 g/100 in²/day
25 µm film; ASTM E-96-92
Oxygen Transmission 9.90 cc-mm/m²-24hr-atm
25.1 cc-mil/100 in²-24hr-atm
25 µm film; ASTM D1434-82; 50% RH
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 69.0 MPa
10000 psi
25 µm film; 3% yield point, orientation not specified; ASTM D882-91
Film Elongation at Break, MD 75 %
75 %
Orientation not specified; ASTM D882
Poissons Ratio 0.34
0.34
Avg. three samples elongated at 5%, 7%, 10%
Secant Modulus 2.80 GPa
406 ksi
ASTM D882
Impact Test 0.780 J
0.575 ft-lb
25 µm film; Impact strength per DuPont Pneumatic Impact Test
Coefficient of Friction, Dynamic 0.48
0.48
film to film; ASTM D1894-90
Coefficient of Friction, Static 0.63
0.63
film to film; ASTM D1894-90
Film Tensile Strength at Break, MD 221 MPa
32100 psi
Orientation not specified; ASTM D882
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature -14.0 - 38.0 °C
11.1 µin/in-°F

@Temperature 6.80 - 100 °F
25 µm film; ASTM D696-91
32.0 µm/m-°C

@Temperature 100 - 200 °C
17.8 µin/in-°F

@Temperature 212 - 392 °F
25 µm film
40.0 µm/m-°C

@Temperature 200 - 300 °C
22.2 µin/in-°F

@Temperature 392 - 572 °F
25 µm film
Specific Heat Capacity 1.09 J/g-°C
0.261 BTU/lb-°F
Differential Calorimetry
Thermal Conductivity 0.120 W/m-K
0.833 BTU-in/hr-ft²-°F
ASTM F433-77
Maximum Service Temperature, Air 400 °C
752 °F
Kapton® can function after brief exposure to 400°C (750°F). Various grades are UL rated for continuous service at 220-240°C (430-460°F).
Minimum Service Temperature, Air -269 °C
-452 °F
Maintains properties and flexibility
Glass Transition Temp, Tg 360 - 410 °C
680 - 770 °F
A 2<sup>nd</sup> order transition occurs in Kapton® between 360-410°C (680-770°F) and is assumed to be the T<sub>g</sub>
Flammability, UL94 V-0
V-0
Optical Properties Metric English Comments
Refractive Index 1.70

@Wavelength 589.3 nm
1.70

@Wavelength 589.3 nm
Na D line; ASTM D542-90
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
in damp heat; IPC-TM-650; Method 2.5.17
1.50e+17 ohm-cm
1.50e+17 ohm-cm
per ASTM D257-91
Dielectric Constant 3.5

@Frequency 100000 Hz
3.5

@Frequency 100000 Hz
3.6

@Frequency 1000 Hz
3.6

@Frequency 1000 Hz
Use evaporated metal electrodes, two terminal system of measurement at standard conditions.; ASTM D150
Dielectric Strength 217 kV/mm
5510 kV/in
Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
Same test as dielectric constant.
0.0090

@Frequency 100000 Hz
0.0090

@Frequency 100000 Hz