DSM Novamid® 1010C2 PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010C2 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy Molding Grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 3.30 % | 3.30 % | Sim. To ISO 62 |
| Viscosity Test | 118 cm³/g | 118 cm³/g | Viscosity Number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | cond; ISO 527-1/-2 |
| 87.0 MPa | 12600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 18 % | 18 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 4.2 % | 4.2 % | dry; ISO 527-1/-2 |
| 21 % | 21 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 1.70 GPa | 247 ksi | cond; ISO 527-1/-2 |
| 3.40 GPa | 493 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 49.0 MPa | 7110 psi | cond; ISO 178 |
| 112 MPa | 16200 psi | dry; ISO 178 | |
| Flexural Modulus | 1.00 GPa | 145 ksi | cond; ISO 178 |
| 2.80 GPa | 406 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.440 J/cm² @Temperature 23.0 °C |
2.09 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 2.60 J/cm² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 2.00e+14 ohm | 2.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.023 @Frequency 1.00e+6 Hz |
0.023 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- MV Labs AS600 AsI3 Arsenic(III) iodide
- Nye Lubricants 230F Oil
- Kennametal Stellite Stellite® 238 Cobalt Alloy
- SABIC Innovative Plastics Valox® V9260CS PET (Europe-Africa-Middle East)
- Teknor Apex Uniprene® UN-7010-64NT Thermoplastic Vulcanizate
- United Cast Bar Unibar 250 Continuously Cast Iron
- Hexcel® HexPly® F650 Bismaleimide Resin with T300 Fiber
- DuPont Performance Polymers Crastin® SK609 NC010 PBT (Unverified Data**)
- Axiall EX 3114B Plenum Flexible PVC
- Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding
Copyright © lookpolymers.com All Rights Reserved