- Diamond Polymers ABS 3500
Diamond Polymers ABS 3500
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3500.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Natural, Injection Molding Grade, Medium ImpactInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.9 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.9 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
8.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 34.9 MPa | 5060 psi | chs 2 in/min; ASTM D638 |
| Tensile Strength, Yield | 43.2 MPa | 6270 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 43 % | 43 % | chs 2 in/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.35 GPa | 341 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
3.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 107 °C | 224 °F | 0.125 inch, 1 Kg, 2°C/minute; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Nitriflex NitriClean 3350X NBR - Nitrile Rubber
- Pau Tai UNISTAB MS-63 Solid Complex Stabilizer
- Lucent Polymers ABS-305 Acrylonitrile Butadiene Styrene, General Purpose
- Stellarchem LP-845 TPE Compound
- Unitika A1030FR PA6, Dry
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N220 Filler
- DuPont Teijin Films Melinex® 544 Polyester Film, 380 Gauge
- SABIC Innovative Plastics Valox® VGF4715 PBT (Asia Pacific)
- Johnson Matthey Matti-phos 5 Alloy for Fluxless Brazing of Copper
- PolyOne Edgetek® AM-20CF-20GF/000 Polyphthalamide (PPA), Glass/Carbon Fiber Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved