DSM EcoPaXX® Q150-D PA410
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q150-D PA410.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low/Medium Viscosity
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.00 % | 2.00 % | Sim. To ISO 62 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | Viscosity Number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | cond; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 16 % | 16 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| 16 % | 16 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 1.70 GPa | 247 ksi | cond; ISO 527-1/-2 |
| 3.10 GPa | 450 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 55.0 MPa | 7980 psi | cond; ISO 178 |
| 115 MPa | 16700 psi | dry; ISO 178 | |
| Flexural Modulus | 1.45 GPa | 210 ksi | cond; ISO 178 |
| 2.90 GPa | 421 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | dry; ISO 75-1/-2 |
| Glow Wire Test | 825 °C @Thickness 0.800 mm |
1520 °F @Thickness 0.0315 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 |
| 850 °C @Thickness 0.800 mm |
1560 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature, dry; IEC 60695-2-13 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 70 | ASTM 6866 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ PA6/6 SI2 FD WH Flame Retardant
- NIZHNEKAMSKNEFTEKHIM PE 4131L (314F4) Linear Low Density Polyethylene
- Albis Plastics Cellulose Acetate Butyrate B9324 (UVI, Odor Mask Added), 4% Plasticizer (discontinued **)
- Michelman® Michem® Emulsion 93135M Nonionic polyethylene emulsion
- SABIC Innovative Plastics LNP Thermocomp FF001 PE (Europe-Africa-Middle East)
- Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate
- Borealis Visico™ ME4425/LE4432 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation
- Williams Advanced Alloys C105 Solder
- ExxonMobil LL 1107x93 Blown Film Resin
- API Megol AM SV/PS SEBS Adhesion Modified Overmolding for PS
Copyright © lookpolymers.com All Rights Reserved