DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer DuPont Performance Polymers
Trade Name Minlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Mineral Reinforced Polyamide 6 Minlon 73M30 NC010 is a 30% mineral reinforced heat stabilized polyamide 6 resin for injection molding. It has isotropic properties and low warpage.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
DAM; ISO 1183
Water Absorption 6.3 %

@Thickness 2.00 mm
 6.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.10 %

@Thickness 2.00 mm
 2.10 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50%RH; ISO 527-1/-2
82.0 MPa
11900 psi
DAM; ISO 527-1/-2
Tensile Stress 5.15 MPa

@Strain 1.23 %,
Temperature 150 °C
 747 psi

@Strain 1.23 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
6.35 MPa

@Strain 1.21 %,
Temperature 150 °C
 921 psi

@Strain 1.21 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
7.66 MPa

@Strain 1.22 %,
Temperature 90.0 °C
 1110 psi

@Strain 1.22 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
9.69 MPa

@Strain 1.21 %,
Temperature 90.0 °C
 1410 psi

@Strain 1.21 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
12.15 MPa

@Strain 4.83 %,
Temperature 150 °C
 1762 psi

@Strain 4.83 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
12.49 MPa

@Strain 1.23 %,
Temperature 40.0 °C
 1812 psi

@Strain 1.23 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
15.06 MPa

@Strain 4.82 %,
Temperature 150 °C
 2184 psi

@Strain 4.82 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
15.07 MPa

@Strain 8.43 %,
Temperature 150 °C
 2186 psi

@Strain 8.43 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
17.24 MPa

@Strain 1.23 %,
Temperature 23.0 °C
 2500 psi

@Strain 1.23 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
18.34 MPa

@Strain 4.81 %,
Temperature 90.0 °C
 2660 psi

@Strain 4.81 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
18.84 MPa

@Strain 8.43 %,
Temperature 150 °C
 2733 psi

@Strain 8.43 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
19.91 MPa

@Strain 0.390 %,
Temperature 0.000 °C
 2888 psi

@Strain 0.390 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
20.0 MPa

@Strain 0.390 %,
Temperature -20.0 °C
 2900 psi

@Strain 0.390 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
23.41 MPa

@Strain 8.45 %,
Temperature 90.0 °C
 3395 psi

@Strain 8.45 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
23.61 MPa

@Strain 4.83 %,
Temperature 90.0 °C
 3424 psi

@Strain 4.83 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
28.29 MPa

@Strain 4.85 %,
Temperature 40.0 °C
 4103 psi

@Strain 4.85 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
29.8 MPa

@Strain 8.45 %,
Temperature 90.0 °C
 4320 psi

@Strain 8.45 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
33.03 MPa

@Strain 12.0 %,
Temperature 90.0 °C
 4791 psi

@Strain 12.0 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
34.96 MPa

@Strain 4.83 %,
Temperature 23.0 °C
 5071 psi

@Strain 4.83 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
35.15 MPa

@Strain 8.40 %,
Temperature 40.0 °C
 5098 psi

@Strain 8.40 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
36.63 MPa

@Strain 0.770 %,
Temperature 23.0 °C
 5313 psi

@Strain 0.770 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
37.44 MPa

@Strain 1.12 %,
Temperature 0.000 °C
 5430 psi

@Strain 1.12 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
38.64 MPa

@Strain 12.02 %,
Temperature 40.0 °C
 5604 psi

@Strain 12.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
39.21 MPa

@Strain 1.21 %,
Temperature 40.0 °C
 5687 psi

@Strain 1.21 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
39.47 MPa

@Strain 0.740 %,
Temperature -20.0 °C
 5725 psi

@Strain 0.740 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
42.58 MPa

@Strain 8.43 %,
Temperature 23.0 °C
 6176 psi

@Strain 8.43 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
46.36 MPa

@Strain 12.02 %,
Temperature 23.0 °C
 6724 psi

@Strain 12.02 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
60.98 MPa

@Strain 4.29 %,
Temperature 0.000 °C
 8844 psi

@Strain 4.29 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
63.77 MPa

@Strain 1.33 %,
Temperature -20.0 °C
 9249 psi

@Strain 1.33 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
66.1 MPa

@Strain 7.51 %,
Temperature 0.000 °C
 9590 psi

@Strain 7.51 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
69.07 MPa

@Strain 10.74 %,
Temperature 0.000 °C
 10020 psi

@Strain 10.74 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
70.63 MPa

@Strain 1.54 %,
Temperature 0.000 °C
 10240 psi

@Strain 1.54 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
84.89 MPa

@Strain 2.97 %,
Temperature -20.0 °C
 12310 psi

@Strain 2.97 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
85.21 MPa

@Strain 3.03 %,
Temperature 23.0 °C
 12360 psi

@Strain 3.03 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
87.74 MPa

@Strain 1.98 %,
Temperature -20.0 °C
 12730 psi

@Strain 1.98 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
88.69 MPa

@Strain 5.16 %,
Temperature -20.0 °C
 12860 psi

@Strain 5.16 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
96.16 MPa

@Strain 2.69 %,
Temperature 0.000 °C
 13950 psi

@Strain 2.69 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
103.22 MPa

@Strain 2.65 %,
Temperature -20.0 °C
 14971 psi

@Strain 2.65 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
2.40 MPa

@Strain 0.360 %,
Time 3.60e+7 sec
 348 psi

@Strain 0.360 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
2.40 MPa

@Strain 0.201 %,
Time 3600 sec
 348 psi

@Strain 0.201 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
2.40 MPa

@Strain 0.287 %,
Time 360000 sec
 348 psi

@Strain 0.287 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
2.40 MPa

@Strain 0.324 %,
Time 3.60e+6 sec
 348 psi

@Strain 0.324 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
2.40 MPa

@Strain 0.244 %,
Time 36000 sec
 348 psi

@Strain 0.244 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
9.60 MPa

@Strain 1.23 %,
Time 360000 sec
 1390 psi

@Strain 1.23 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
9.60 MPa

@Strain 0.874 %,
Time 3600 sec
 1390 psi

@Strain 0.874 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
9.60 MPa

@Strain 1.51 %,
Time 3.60e+7 sec
 1390 psi

@Strain 1.51 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
9.60 MPa

@Strain 1.05 %,
Time 36000 sec
 1390 psi

@Strain 1.05 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
9.60 MPa

@Strain 1.37 %,
Time 3.60e+6 sec
 1390 psi

@Strain 1.37 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
19.2 MPa

@Strain 3.28 %,
Time 3.60e+6 sec
 2780 psi

@Strain 3.28 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
19.2 MPa

@Strain 2.64 %,
Time 36000 sec
 2780 psi

@Strain 2.64 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
19.2 MPa

@Strain 3.54 %,
Time 3.60e+7 sec
 2780 psi

@Strain 3.54 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
19.2 MPa

@Time 3600 sec,
Strain 2.23 %
 2780 psi

@Time 1.00 hour,
Strain 2.23 %
 50%RH; isochronous; ISO 11403-1 -2
19.2 MPa

@Strain 3.00 %,
Time 360000 sec
 2780 psi

@Strain 3.00 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 15 %
15 %
DAM; ISO 527-1/-2
40 %
40 %
50%RH; ISO 527-1/-2
Tensile Modulus 1.70 GPa
247 ksi
50%RH; ISO 527-1/-2
4.80 GPa
696 ksi
DAM; ISO 527-1/-2
0.443 GPa

@Temperature 150 °C
 64.3 ksi

@Temperature 302 °F
 50%RH; ISO 11403-1 -2