- Covestro Bayblend® T45 Polycarbonate + ABS
Covestro Bayblend® T45 Polycarbonate + ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® T45 Polycarbonate + ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose injection molding gradeVicat/B 120 temperature = 112 °CPreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| 0.935 g/cc @Temperature 260 °C |
0.0338 lb/in³ @Temperature 500 °F |
Melt | |
| Water Absorption | 0.70 % | 0.70 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527-1/-2 |
| Elongation at Yield | 3.7 % | 3.7 % | ISO 527-1/-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.76 J/g-°C | 0.421 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.142 W/m-K | 0.985 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
| Vicat Softening Point | 110 °C | 230 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.900 mm |
HB @Thickness 0.0354 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0035 @Frequency 100 Hz |
0.0035 @Frequency 100 Hz |
IEC 60250 |
| 0.0085 @Frequency 1.00e+6 Hz |
0.0085 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| 260 °C | 500 °F | Injection Molding; ISO 294 | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 80.0 °C | 176 °F | Injection Molding; ISO 10724 | |
| Ejection Temperature | 110 °C | 230 °F | |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | North America | |
| Eff. thermal diffusivity (m²/s) | 8.63E-08 | |
| Feature | Release agent | |
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa EDISTIR PD RK4514H High Impact Polystyrene (HIPS) (discontinued **)
- SABIC Innovative Plastics Lexan® HFD4211 PC (Europe-Africa-Middle East)
- FKuR Kunststoff Bio-Flex® F 1110 Compostable PLA Blend
- GRECO ISOPAK 525 ABS Resin
- Lubrizol Advanced Materials Pearlbond® 580 Thermoplastic Polyurethane
- Tra-Con Tra-Bond 2125NB Repair Epoxy Adhesive
- Eurostar Starflam PX07037 PA6, Flame Retardant, Injection Molded
- Covestro Bayflex® MP-5000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Fainplast Compounds PH 74/AL Flexible PVC, Transparent Extrusion
- Plaskolite West Optix® CA - 71 General Purpose Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved