Covestro Apec® 2097 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Covestro |
| Trade Name | Apec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Apec® 2097 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowingeasy to demoldUV-stabilizedsoftening temperature (VST/B 120)=202 °CPreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| 0.970 g/cc @Temperature 330 °C |
0.0350 lb/in³ @Temperature 626 °F |
Melt | |
| Water Absorption | 0.30 % | 0.30 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | Similar to ISO 62 |
| Melt Flow | 7.8 g/10 min @Load 2.16 kg, Temperature 330 °C |
7.8 g/10 min @Load 4.76 lb, Temperature 626 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 6.9 % | 6.9 % | ISO 527-1/-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Impact | 5200 | 5200 | Puncture - maximum force (N); ISO 6603-2 |
| 6000 @Temperature -30.0 °C |
6000 @Temperature -22.0 °F |
Puncture - maximum force (N); ISO 6603-2 | |
| Puncture Energy | 55.0 J | 40.6 ft-lb | ISO 6603-2 |
| 60.0 J @Temperature -30.0 °C |
44.3 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.165 W/m-K | 1.15 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 0.46 MPa (66 psi) | 191 °C | 376 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Oxygen Index | 25 % | 25 % | ISO 4589-1/-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | transparent; thickness unknown |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
IEC 60250 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00070 @Frequency 100 Hz |
0.00070 @Frequency 100 Hz |
IEC 60250 |
| 0.0080 @Frequency 1.00e+6 Hz |
0.0080 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 330 °C | 626 °F | Injection Molding; ISO 294 |
| 330 - 340 °C | 626 - 644 °F | ||
| Mold Temperature | 100 °C | 212 °F | Injection Molding; ISO 10724 |
| 130 - 150 °C | 266 - 302 °F | ||
| Ejection Temperature | 183 °C | 361 °F | |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Europe | |
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Eff. thermal diffusivity (m²/s) | 1E-07 | |
| Feature | Release agent | |
| U.V. stabilised or stable to weather | ||
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- Ovation Polymers Optrene 10GF Polypropylene
- LG Chemical AF360C ABS, TBBA-free Flame Retardant, High Flow
- Heatbath/Park Carbon Cover
- Chengdu Polyster 5500 General Grade TPV
- ChevronTexaco CP Grease
- Daikin DAI-EL G-716 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- Denka VINYKON W4029 PVC, W grade for equipment cords, for heat resistance
- Akzo Nobel Trigonox® EHP Polymerization Initiator
- Teknor Apex APEX® 2565-H Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved