Haysite ETS-FR-II Glass Reinforced Polyester Sheet, Electrical Grade (GPO2)

Category	Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass SMC
Manufacturer	Haysite
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Haysite ETS-FR-II Glass Reinforced Polyester Sheet, Electrical Grade (GPO2).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A NEMA GPO-2 glass mat reinforced thermoset polyester molded sheet. ETS-FR-II is UL recognized with a flame rating of 94V-0 and arc resistance of 185 seconds. This grade is an IEEE Thermal Class B, 130ÂºC electrical/160ÂºC mechanical material. Typical uses are general purpose electrical insulation application where flame retardancy is required. Available thicknesses - .032" - 2.00". Standard color - Red. Meets Gov't Specs - LP-509, I-24768/6.

Physical Properties	Metric	English	Comments
Density	1.84 g/cc	0.0665 lb/inÂ³	ASTM D572
Water Absorption	0.20 %	0.20 %	ASTM D570

Mechanical Properties	Metric	English	Comments
Hardness, Barcol	46	46
Tensile Strength, Ultimate	69.0 MPa	10000 psi
Flexural Strength	145 MPa	21000 psi
Flexural Modulus	6.90 GPa	1000 ksi
Compressive Strength	207 MPa	30000 psi
Shear Strength	97.0 MPa	14100 psi	ASTM D732
Izod Impact, Notched	4.30 J/cm	8.06 ft-lb/in	edgewise; ASTM D256

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	130 Â°C	266 Â°F	Approximate temperature class
Flammability, UL94	V-0	V-0	File No.E81893

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.4 @Frequency 60 Hz	4.4 @Frequency 60 Hz	ASTM D150
Dielectric Strength	22.0 kV/mm @Thickness 1.59 mm	559 kV/in @Thickness 0.0625 in	Perpendicular, Short Time in Oil and Air; ASTM D149
Dissipation Factor	0.031 @Frequency 60 Hz	0.031 @Frequency 60 Hz	ASTM D150
Arc Resistance	180 sec	180 sec	ASTM D495
Comparative Tracking Index	>= 500 V	>= 500 V