Cossa Polimeri ESTADIENE 0425 GFS Acrylonitrile Butadiene Styrene, 13% Glass Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTADIENE
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Cossa Polimeri ESTADIENE 0425 GFS Acrylonitrile Butadiene Styrene, 13% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
ABS with 13% short glass fiberExcellent mechanical and thermal propertiesInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D 955
Melt Flow 4.0 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 4.0 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 26.0 MPa
3770 psi
ASTM D 638
Tensile Strength, Yield 28.0 MPa
4060 psi
ASTM D 638
Elongation at Break 2.0 %
2.0 %
ASTM D 638
Flexural Modulus 2.60 GPa
377 ksi
ASTM D 790
Izod Impact, Notched 1.50 J/cm
<br>@Temperature 0.000 °C
 2.81 ft-lb/in
<br>@Temperature 32.0 °F
 ASTM D 638
1.80 J/cm
<br>@Temperature 23.0 °C
 3.37 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 98.0 °C
<br>@Load 5.00 kg
 208 °F
<br>@Load 11.0 lb
 50°C/hr; ASTM D 1525
107 °C
<br>@Load 0.999 kg
 225 °F
<br>@Load 2.20 lb
 50°C/hr; ASTM D 1525
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in
Glow Wire Test 650 °C
<br>@Thickness 2.00 mm
 1200 °F
<br>@Thickness 0.0787 in
 I.E.C. 695-2-1