SABIC Innovative Plastics LNP THERMOCOMP EC006PXQ PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EC006PXQ PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* EC006PXQ is a compound based on Polyetherimide containing 30% Carbon FIber. Added features include: Electrically Conductive, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00030 - 0.0010 cm/cm @Time 86400 sec |
0.00030 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0060 cm/cm @Time 86400 sec |
0.0010 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 22 g/10 min @Load 6.70 kg, Temperature 380 °C |
22 g/10 min @Load 14.8 lb, Temperature 716 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 248 MPa | 36000 psi | 5 mm/min; ISO 527 |
| 272 MPa | 39500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.3 - 1.4 % | 1.3 - 1.4 % | Type I, 5 mm/min; ASTM D638 | |
| 334 % | 334 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 27.56 GPa | 3997 ksi | 1 mm/min; ISO 527 |
| 29.52 GPa | 4282 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 341 MPa | 49500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 23.06 GPa | 3345 ksi | 2 mm/min; ISO 178 |
| 23.8 GPa | 3450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Compressive Strength | 244 MPa | 35400 psi | SABIC Method |
| Poissons Ratio | 0.44 | 0.44 | ASTM E 132 |
| Shear Modulus | 4.726 GPa | 685.5 ksi | ASTM C273 |
| Shear Strength | 128 MPa | 18600 psi | ASTM C273 |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.81 J/cm | 10.9 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C @Temperature -40.0 - 150 °C |
3.89 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 8.00 µm/m-°C @Temperature -40.0 - 150 °C |
4.44 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 5100 (SVLG) Synthetic Oil
- NanoAmor 95%, OD: 30-50 nm OH Functionalized Aligned Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics Lexan® FXD123R PC (Europe-Africa-Middle East)
- Pau Tai Cadmium stearate, Monomer Stabilizer
- Sinotek Materials R20 C Carbon Rod for Dry Battery
- Samyang Tribit® 1500G10 PBT, Reinforced General Purpose
- Zotefoams Evazote® EV30 Ethylene Vinyl Acetate Copolymer Foam
- DuPont Performance Polymers Delrin® 500P BK602 Acetal (POM) (Unverified Data**)
- ExxonMobil Mobil Nyvac FR 200D
- Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved