Aclo Accutech Polypropylene Homopolymer HP0336W40L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336W40L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 68 | 68 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ASTM D638 |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Flexural Modulus | 4.300 GPa | 623.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F |
Users viewing this material also viewed the following:
- RheTech Products HP800-706UV 20% Talc Reinforced High Performance Polypropylene Copolymer, Scratch Resistant, UV Stabilized, Impact Modified, SWB White
- SABIC Innovative Plastics Lexan® ML6411 PC Copolymer (Asia Pacific)
- 3M Dyneon™ Aflas® FA-150L PTFE Fluoroelastomer (discontinued **)
- Parker Chomerics CHO-SEAL 1273 Conductive Elastomer
- Shuman 790 Black and Custom Colors ABS-Flame Retardant
- ExxonMobil 424 Mobilmet 400 Series
- Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
- ATI Allegheny Ludlum Moly Permalloy Electrical Alloy
- PolyOne Geon™ Vinyl Wire & Cable W1202 Polyvinyl Chloride, Flexible (PVC, Flexible)
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved