Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | |
| Apparent Bulk Density | 0.300 g/cc | 0.0108 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
| Flexural Strength | 103 MPa | 14900 psi | |
| Compressive Strength | 186 MPa | 27000 psi | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
Wet |
| 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Wet |
| 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 160 sec | 160 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Omya OMYAFIL® Calcium Carbonate
- Polymer Resources NY66-FRG25 Flame Retardant Nylon 66, 25% Glass Reinforced
- Hong Kun Group HOBt, Anhydrous Pharmaceutical Intermediate
- Kobe Steel KS15-3-3-3 Beta Titanium Alloy, AMS 4914, Solution treated and aged 482°C, 16 hrs - AC
- Huntsman AVALON® 650 B Thermoplastic Polyurethane
- LATI Latilon 28D G/20 PC, 20% Glass Fiber Reinforced
- Schott Glass 8660 Borosilicate Glass
- Chase Plastics CP Pryme® N340MGL (DAM) Nylon 6 (Utility Grade), 40% Mineral/Glass Fiber Reinforced, Internally Lubricated
- American Elements Molybdenum Oxide Nanopowder
- Compuestos Dominicanos Polycom VN-051090 PVC Compound
Copyright © lookpolymers.com All Rights Reserved